三方相0.95Pb(Zn1/3Nb2/3)O3–0.05PTiO3单晶的相转变特性与电学性能研究 | |
Fang BJ ; Pan SS ; Du QB ; 赵祥永 ; 徐海清 ; 罗豪甦 | |
刊名 | Journal of the Physical Society of Japan
![]() |
2010-09-27 | |
卷号 | 79期号:10页码:104703-104709 |
ISSN号 | 0031-9015 |
其他题名 | Phase Transition Character and Electrical Properties of Rhombohedral 0.95Pb(Zn1/3Nb2/3)O3–0.05PTiO3 Single Crystals |
通讯作者 | 方必军 |
中文摘要 | Large-size and high-quality 0.95Pb(Zn1/3Nb2/3)O3–0.05PbTiO3 (0.95PZN–0.05PT) single crystals were grown by a modified Bridgman method using an allomeric 0.69Pb(Mg1/3Nb2/3)O3–0.31PbTiO3 single crystal as a seed. The as-grown 0.95PZN–0.05PT single crystals exhibit rhombohedral perovskite structure, which changes wholly into cubic structure at 165 C confirmed by high-temperature X-ray diffraction measurement. 0.95PZN–0.05PT exhibits broad and diffused dielectric response peaks accompanied by apparent dielectric frequency dispersion. Polarization induces an additional dielectric anomaly around 109 C accompanied by the increase of the temperature of dielectric maximum (Tm),decrease of the value of dielectric maximum ("m) and the enhancement of frequency dispersion which can be assigned to the orientation of ferroelectric domain or a macro–micro domain transition upon heating. The [001]-oriented 0.95PZN–0.05PT crystals exhibit excellent electrical properties, where remanent polarization Pr is 36.89 mC/cm2 and piezoelectric constant d33 is around 1120–1180 pC/N.Pyroelectric coefficient p, detectivity and voltage responsivity figures of merit Fd and Fv of the 0.95PZN–0.05PT single crystals are 458 mC/(K m2), 6.027 mPa 1=2, and 0.0125m2/C, respectively,which increase greatly over the temperature range measured. It is needed to improve temperature stability and voltage responsivity to meet the requirements of practical applications. 0.95PZN–0.05PT exhibits rather high transparency, with the ultraviolet cut-off edge near 385 nm indicating a low-lying electronic energy gap of 3:12 eV. The infrared-absorption band occurs at 595 cm 1, which can be attributed to the normal vibration of (Zn1/3Nb2/3)/TiO3 group. |
学科主题 | 材料科学 |
收录类别 | SCI收录 |
语种 | 英语 |
公开日期 | 2012-07-05 |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/1199] ![]() |
专题 | 上海硅酸盐研究所_无机功能材料与器件重点实验室_期刊论文 |
推荐引用方式 GB/T 7714 | Fang BJ,Pan SS,Du QB,等. 三方相0.95Pb(Zn1/3Nb2/3)O3–0.05PTiO3单晶的相转变特性与电学性能研究[J]. Journal of the Physical Society of Japan,2010,79(10):104703-104709. |
APA | Fang BJ,Pan SS,Du QB,赵祥永,徐海清,&罗豪甦.(2010).三方相0.95Pb(Zn1/3Nb2/3)O3–0.05PTiO3单晶的相转变特性与电学性能研究.Journal of the Physical Society of Japan,79(10),104703-104709. |
MLA | Fang BJ,et al."三方相0.95Pb(Zn1/3Nb2/3)O3–0.05PTiO3单晶的相转变特性与电学性能研究".Journal of the Physical Society of Japan 79.10(2010):104703-104709. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论