Laser welding of TiNi shape memory alloy and stainless steel using Ni interlayer | |
Li HM ; Sun DQ ; Cai XL ; Dong P ; Wang WQ | |
刊名 | materials & design |
2012 | |
卷号 | 39页码:285-293 |
关键词 | MICROSTRUCTURE PARAMETERS WIRES |
ISSN号 | 0261-3069 |
通讯作者 | sun dq |
中文摘要 | laser welding of tini shape memory alloy wire to stainless steel wire using ni interlayer was investigated. the results indicated that the ni interlayer thickness had great effects on the chemical composition, microstructure, gas-pore susceptibility and mechanical properties of laser-welded joints. with an increase of ni interlayer thickness, the weld ni content increased and the joint properties increased due to decreasing brittle intermetallic compounds (tife2 and ticr2). the joint fracture occurred in the fusion zone with a brittle intermetallic compound layer. the tensile strength and elongation of the joints reached the maximum values (372 mpa and 4.4%) when weld ni content was 47.25 wt.%. further increasing weld ni content resulted in decreasing the joint properties because of forming more tini3 phase, gas-pores and shrinkage cavities in the weld metals. it is necessary to select suitable ni interlayer thickness ( weld composition) for improving the mechanical properties of laser-welded joints. (c) 2012 elsevier ltd. all rights reserved. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000303113900033 |
公开日期 | 2013-04-23 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/48032] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Li HM,Sun DQ,Cai XL,et al. Laser welding of TiNi shape memory alloy and stainless steel using Ni interlayer[J]. materials & design,2012,39:285-293. |
APA | Li HM,Sun DQ,Cai XL,Dong P,&Wang WQ.(2012).Laser welding of TiNi shape memory alloy and stainless steel using Ni interlayer.materials & design,39,285-293. |
MLA | Li HM,et al."Laser welding of TiNi shape memory alloy and stainless steel using Ni interlayer".materials & design 39(2012):285-293. |