Growth and spectroscopic properties of Nd3+/Yb3+-codoped Sr3Gd2(BO3)(4) crystal

	Growth and spectroscopic properties of Nd3+/Yb3+-codoped Sr3Gd2(BO3)(4) crystal
	H. Wu ; L. Zhang ; Z. Lin ; G. Wang
刊名	Materials Research Innovations
	2007-03
卷号	11 期号:1 页码:31-36
关键词	Nd3+/Yb3+: Sr3Gd2(BO3)(4) crystal crystal growth spectral properties Judd-Ofelt theory optical-transition probability rare-earth ions spectral parameters nd3+ ion yb3+ ions laser yag intensities absorption
ISSN号	1432-8917
中文摘要	A Nd3+/Yb3+ : Sr3Gd2(BO3)(4) crystal 40 mm in diameter and 15 mm in height was grown by the Czochralski method. The spectroscopic characterization of Nd3+/Yb3+:Sr3Gd2(BO3)(4) crystal was investigated. The emission crosssection of Yb3+ in the Nd3+/Yb3(+):Sr3Gd2(BO3)(4) crystal is 1.57 x 10(-20) cm(2) at 1014 nm, and the radiation lifetime tau(rad) of F-2(5/2) of Yb3+ is 881.6 mu s. The result shows that the energy transfer occurs from F-4(3/2) of Nd3+ to F-2(5/2) of Yb3+ in the Nd3+/Yb3+:Sr3Gd2(BO3)(4) crystal, which should enhance the laser efficiency of Yb3+ in the Nd3+/Yb3+:Sr3Gd2(BO3)(4) crystal.
语种	英语
公开日期	2013-04-01
内容类型	期刊论文
源URL	[http://ir.fjirsm.ac.cn/handle/350002/6739]
专题	福建物质结构研究所_中科院福建物质结构研究所_期刊论文
推荐引用方式 GB/T 7714	H. Wu,L. Zhang,Z. Lin,et al. Growth and spectroscopic properties of Nd3+/Yb3+-codoped Sr3Gd2(BO3)(4) crystal[J]. Materials Research Innovations,2007,11(1):31-36.
APA	H. Wu,L. Zhang,Z. Lin,&G. Wang.(2007).Growth and spectroscopic properties of Nd3+/Yb3+-codoped Sr3Gd2(BO3)(4) crystal.Materials Research Innovations,11(1),31-36.
MLA	H. Wu,et al."Growth and spectroscopic properties of Nd3+/Yb3+-codoped Sr3Gd2(BO3)(4) crystal".Materials Research Innovations 11.1(2007):31-36.