	Facile synthesis of CNTs-doped diamond-like carbon ﬁlm by electrodeposition
	Zhang JY(张俊彦); Zhang JY(张俊彦)
刊名	Surface and Coatings Technology
	2008
卷号	202 页码:5943-5946
关键词	CNTs DLC ﬁlm Electrodeposition Raman Hardness Residual stress
ISSN号	0257-8972
通讯作者	张俊彦
中文摘要	A simple and effective process for synthesis of carbon nanotubes (CNTs)-doped diamond-like carbon (DLC) ﬁlm via electrodeposition has been reported. Transmission electron microscope (TEM), Raman, X-ray photoelectron spectroscopy (XPS), and Fourier transformation infrared spectrometry (FTIR) were employed to investigate the microstructure, chemical composition, and various carbon phases of the ﬁlms. The experimental results clearly showed that the CNTs were well dispersed in the carbon ﬁlm and the D and G bands of the composite carbon ﬁlm both downshifted comparing with those of the undoped carbon ﬁlm. The hardness of the carbon ﬁlm was improved with the incorporation of CNTs from 10.28 to 12.47 GPa, while the Young's modulus was decreased from 253.64 to 206.66 GPa. Simultaneously, the residual stress of the carbon ﬁlm was greatly reduced from 1.2 to 0.83 GPa after the incorporation of CNTs.
学科主题	材料科学与物理化学
收录类别	SCI
资助信息	the National Natural Science Foundation of China (NSFC) with grant No. 50572108
语种	英语
公开日期	2013-03-28
内容类型	期刊论文
源URL	[http://210.77.64.217/handle/362003/2695]
专题	兰州化学物理研究所_固体润滑国家重点实验室
通讯作者	Zhang JY(张俊彦); Zhang JY(张俊彦)
推荐引用方式 GB/T 7714	Zhang JY,Zhang JY. Facile synthesis of CNTs-doped diamond-like carbon ﬁlm by electrodeposition[J]. Surface and Coatings Technology,2008,202:5943-5946.
APA	张俊彦,&张俊彦.(2008).Facile synthesis of CNTs-doped diamond-like carbon ﬁlm by electrodeposition.Surface and Coatings Technology,202,5943-5946.
MLA	张俊彦,et al."Facile synthesis of CNTs-doped diamond-like carbon ﬁlm by electrodeposition".Surface and Coatings Technology 202(2008):5943-5946.