Synthesis and characterization of a novel poly(arylene ether sulfone) containing pendent imidazole groups for high temperature proton exchange membranes | |
Wang J ; Zheng JF ; Zhao Z ; Zhang SB | |
刊名 | journal of materials chemistry
![]() |
2012 | |
卷号 | 22期号:42页码:22706-22712 |
关键词 | FUEL-CELL APPLICATIONS POLYMER ELECTROLYTE CROSS-LINKING POLYBENZIMIDAZOLE MEMBRANES PHOSPHORIC-ACID AROMATIC POLYETHERS |
ISSN号 | 0959-9428 |
通讯作者 | zhang sb |
中文摘要 | a series of poly(arylene ether sulfone) containing pendent imidazole groups (psf-im-x) have been successfully synthesized based on a novel monomer 2,2'-bis-(2-methyl-imidazol-1-yl-methyl)-biphenyl-4,4'-diol (mipo). the pendent imidazole groups along the polymer chain were expected to provide functional sites for the acid-base interaction with the doping phosphoric acid (pa) when they are used as polymer electrolyte membranes for high temperature fuel cell applications. the pa content of the linear psf-im-x membranes is about 172.3-235.8% in 85 wt% h3po4 at room temperature. the volume swelling of these membranes is 114.4-194.0%, lower than that of polybenzimidazole (pbi) with similar pa content. the proton conductivities of the membranes are 0.021-0.053 s cm(-1) at 140 degrees c under absolutely dehydrated state. the low volume swelling and good proton conductivity may be attributed to the "side-chain-type" structures of pendent imidazole groups, which facilitate ion transport. to obtain higher acid doping while maintaining mechanical properties, cross-linked membranes were prepared by the reaction of the imidazole group of the polymer and p-xylene dichloride. the pa content of the membranes with 20% cross-linking is 313.2% in 85 wt% h3po4 at 80 degrees c. the stress at breaking and the proton conductivity of the membrane is 3.2 mpa at room temperature and 0.063 s cm(-1) at 140 degrees c in an absolutely dehydrated state. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000310721300053 |
公开日期 | 2013-03-18 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/47841] ![]() |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Wang J,Zheng JF,Zhao Z,et al. Synthesis and characterization of a novel poly(arylene ether sulfone) containing pendent imidazole groups for high temperature proton exchange membranes[J]. journal of materials chemistry,2012,22(42):22706-22712. |
APA | Wang J,Zheng JF,Zhao Z,&Zhang SB.(2012).Synthesis and characterization of a novel poly(arylene ether sulfone) containing pendent imidazole groups for high temperature proton exchange membranes.journal of materials chemistry,22(42),22706-22712. |
MLA | Wang J,et al."Synthesis and characterization of a novel poly(arylene ether sulfone) containing pendent imidazole groups for high temperature proton exchange membranes".journal of materials chemistry 22.42(2012):22706-22712. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论