Oxidation behavior of Ni-Al coating with and without a Ni-Re diffusion barrier in dry CO2 gas at 650 degrees C | |
Li, Meifeng; Kong, Charlie; Zhang, Jianqiang; Zhou, Chungen; Young, David J. | |
刊名 | CORROSION SCIENCE |
2019 | |
卷号 | 149页码:236-243 |
关键词 | Ni-Al coating Ni-Re interlayer Inner oxidation CO2 corrosion |
ISSN号 | 0010-938X |
DOI | 10.1016/j.corsci.2019.01.021 |
URL标识 | 查看原文 |
收录类别 | SCIE ; EI |
WOS记录号 | WOS:000459839700023 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/5922450 |
专题 | 北京航空航天大学 |
推荐引用方式 GB/T 7714 | Li, Meifeng,Kong, Charlie,Zhang, Jianqiang,et al. Oxidation behavior of Ni-Al coating with and without a Ni-Re diffusion barrier in dry CO2 gas at 650 degrees C[J]. CORROSION SCIENCE,2019,149:236-243. |
APA | Li, Meifeng,Kong, Charlie,Zhang, Jianqiang,Zhou, Chungen,&Young, David J..(2019).Oxidation behavior of Ni-Al coating with and without a Ni-Re diffusion barrier in dry CO2 gas at 650 degrees C.CORROSION SCIENCE,149,236-243. |
MLA | Li, Meifeng,et al."Oxidation behavior of Ni-Al coating with and without a Ni-Re diffusion barrier in dry CO2 gas at 650 degrees C".CORROSION SCIENCE 149(2019):236-243. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论