Study on nanocrystalline Cr2O3 films deposited by arc ion plating: II. Mechanical and tribological properties | |
T. G. Wang ; D. Jeong ; Y. M. Liu ; Q. Wang ; S. Iyengar ; S. Melin ; K. H. Kim | |
刊名 | Surface & Coatings Technology |
2012 | |
卷号 | 206期号:10页码:2638-2644 |
关键词 | Cr2O3 film Arc ion plating Bias voltage Mechanical property Friction coefficient Wear rate chromium-oxide coatings thin-films tool steel wear behavior temperature performance oxidation corrosion surface |
ISSN号 | 0257-8972 |
中文摘要 | In this work, the influence of substrate bias voltage on the microhardness, adhesive strength, friction coefficient, and wear rate of AIP Cr2O3 films deposited on AISI 304 stainless steel substrates was investigated systematically. In the meantime, the wear failure mechanism of AIP Cr2O3 films in dry sliding contact was also analyzed and discussed. The results showed that the mechanical properties, adhesive behaviors, and tribological performance of AIP Cr2O3 films were greatly altered by applying a negative bias voltage. With increasing the bias voltage, the hardness, critical load, and tribological performance of AIP Cr2O3 films first were improved gradually, and then were impaired slightly again. When the bias voltage is - 100 V. the Cr2O3 film possessed the highest hardness, the strongest adhesion, and the best wear resistance. The essence of above phenomena was attributed to the variations of microstructure and defect density in the films induced by the substrate bias voltage increase. The main wear failure mechanism of AIP Cr2O3 films is crack initiation and propagation under the high contact stresses, inducing the local film with small area to flake off gradually, and eventually leading to the formation of a wear scar. Crown Copyright (C) 2011 Published by Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2013-02-05 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/60306] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | T. G. Wang,D. Jeong,Y. M. Liu,et al. Study on nanocrystalline Cr2O3 films deposited by arc ion plating: II. Mechanical and tribological properties[J]. Surface & Coatings Technology,2012,206(10):2638-2644. |
APA | T. G. Wang.,D. Jeong.,Y. M. Liu.,Q. Wang.,S. Iyengar.,...&K. H. Kim.(2012).Study on nanocrystalline Cr2O3 films deposited by arc ion plating: II. Mechanical and tribological properties.Surface & Coatings Technology,206(10),2638-2644. |
MLA | T. G. Wang,et al."Study on nanocrystalline Cr2O3 films deposited by arc ion plating: II. Mechanical and tribological properties".Surface & Coatings Technology 206.10(2012):2638-2644. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论