Microstructure and properties of aluminum killed low-carbon steel sheets with different thickness during single stand reversing cold rolling | |
Zhuang, Dong-Dong[1]; Wang, Zuo-Cheng[2]; Wang, Lei-Gang[3]; Huang, Yao[4]; Li, Xiao-Min[5]; Zhang, Hua-Yang[6]; Ren, De-Wei[7] | |
刊名 | Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment
![]() |
2015 | |
卷号 | 36页码:45-50 |
ISSN号 | 10096264 |
URL标识 | 查看原文 |
收录类别 | EI ; 中文核心期刊要目总览中国科技核心期刊CSCD |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/5380020 |
专题 | 江苏大学 |
作者单位 | [1]School of Material Science and Engineering, Jiangsu University, Zhenjiang, China [2]School of Material Science and Engineering, Shandong University, Jinan, China [3]School of Material Science and Engineering, Jiangsu University, Zhenjiang, China [4]School of Material Science and Engineering, Jiangsu University, Zhenjiang, China [5]School of Material Science and Engineering, Shandong University, Jinan, China [6]School of Material Science and Engineering, Shandong University, Jinan, China [7]China MCC20 Group Co Ltd, Shanghai, China |
推荐引用方式 GB/T 7714 | Zhuang, Dong-Dong[1],Wang, Zuo-Cheng[2],Wang, Lei-Gang[3],et al. Microstructure and properties of aluminum killed low-carbon steel sheets with different thickness during single stand reversing cold rolling[J]. Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment,2015,36:45-50. |
APA | Zhuang, Dong-Dong[1].,Wang, Zuo-Cheng[2].,Wang, Lei-Gang[3].,Huang, Yao[4].,Li, Xiao-Min[5].,...&Ren, De-Wei[7].(2015).Microstructure and properties of aluminum killed low-carbon steel sheets with different thickness during single stand reversing cold rolling.Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment,36,45-50. |
MLA | Zhuang, Dong-Dong[1],et al."Microstructure and properties of aluminum killed low-carbon steel sheets with different thickness during single stand reversing cold rolling".Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment 36(2015):45-50. |