CORC > 新疆理化技术研究所 > 中国科学院新疆理化技术研究所 > 材料物理与化学研究室

	镍钴酸锂的空气气氛下高温固相合成
	郭红兵; 康雪雅; 王天雕; 韩英
刊名	电子元件与材料
	2005
卷号	24 期号:6 页码:18-20
关键词	无机非金属材料锂离子电池正极材料锂镍钴氧化物
ISSN号	1001-2028
其他题名	study on synthesis of lini0.7co0.3o2 by high temperature solid phase method in atmosphere
中文摘要	通过改进马弗炉结构,在空气气氛下合成了LiNi0.7Co0.3O2锂离子二次电池正极材料。利用XRD、SEM和循环充放电测试等手段,研究了材料结构与电化学性能之间的关系。实验电池以C/3的电流倍率在2.7~4.2V进行恒流充放电循环,电池首次充电比容量与放电比容量分别为181mAh/g和157mAh/g,库仑效率为86.7%。经过15次循环后,放电比容量趋于稳定,库仑效率保持在98%以上。循环40次,放电比容量为122mAh/g。
英文摘要	Using converting the air in muffle sufficiently, LiNio.7Coo.3O2 lithium-ion battery anode materials were synthesized by solid state reaction in air condition. The relationship between material structure and electrochemicat properties were characterized by means of X-ray diffraction (XRD), scanning electron microscope (SEM) and charge-discharge studies. The experiment cells were charged at constant current (C/3) to 4.2 V, after a rest period of 2 min, cells were discharged to 2.7 V at the same constant current (C/3). The specific charge and discharge capacity of the first circle are 181 mAh/g and 157 mAh/g, respectively. And its coulombic efficiency is 86.7%. After the fifteen cycle, the specific discharge capacity gets stably, and the coulombic efficiency of each cycle is over 98%, the specific discharge capacity retains 122 mAh/g in the fortieth cycle.
学科主题	Engineering (provided by Thomson Reuters)
公开日期	2012-11-29
内容类型	期刊论文
源URL	[http://ir.xjipc.cas.cn/handle/365002/2137]
专题	新疆理化技术研究所_材料物理与化学研究室
作者单位	中国科学院新疆理化技术研究所；中国科学院研究生院
推荐引用方式 GB/T 7714	郭红兵,康雪雅,王天雕,等. 镍钴酸锂的空气气氛下高温固相合成[J]. 电子元件与材料,2005,24(6):18-20.
APA	郭红兵,康雪雅,王天雕,&韩英.(2005).镍钴酸锂的空气气氛下高温固相合成.电子元件与材料,24(6),18-20.
MLA	郭红兵,et al."镍钴酸锂的空气气氛下高温固相合成".电子元件与材料 24.6(2005):18-20.