LiAl0.03Mn1.97O4的流变相辅助微波合成及电化学性能 | |
崔涛; 华宁; 韩英; 康雪雅 | |
刊名 | 电子元件与材料
![]() |
2007 | |
卷号 | 26期号:12页码:10-13 |
关键词 | 电子技术 LiAl0.03Mn1.97O4 锂离子电池正极材料 流变相辅助微波合成法 |
中文摘要 | 采用流变相辅助微波合成法,制备了结晶度好、纯度高的尖晶石相的锂离子电池正极材料LiAl0.03Mn1.97O4。对其进行了XRD分析和SEM研究,并与传统固相法制备的LiMn2O4和LiAl0.03Mn1.97O4进行了比较。结果表明,该合成法制备的LiAl0.03Mn1.97O4具有优良的电化学性能,用这种材料制造的电池具有比较高的首次放电容量(115 mAh/g)以及良好的可逆性和循环性能,25次循环后比容量几乎不变,保持在115 mAh/g左右。 |
英文摘要 | The LiAl_(0.03)Mn_(1.97)O_4 used in lithium-ion batteries was synthesized by a rheological-phase-assisted microwave synthesis method.The samples were compared with LiMn_2O_4 and LiAl_(0.03)Mn_(1.97)O_4 obtained from the traditional solid-state reaction method and were investigated by XRD and SEM.The sample was used as cathode material for lithium-ion battery,whose charge/discharge properties and cycle performance were examined.The results reveal that the powder prepared by this method exhibits a higher initial discharge capacity of 115 mAh/g,much better reversibility and good cycling stability,after 25 cycles without discharge capacity fading,retaining 115 mAh/g. |
公开日期 | 2012-11-29 |
内容类型 | 期刊论文 |
源URL | [http://ir.xjipc.cas.cn/handle/365002/2012] ![]() |
专题 | 新疆理化技术研究所_材料物理与化学研究室 |
作者单位 | 中国科学院新疆理化技术研究所;中国科学院研究生院 |
推荐引用方式 GB/T 7714 | 崔涛,华宁,韩英,等. LiAl0.03Mn1.97O4的流变相辅助微波合成及电化学性能[J]. 电子元件与材料,2007,26(12):10-13. |
APA | 崔涛,华宁,韩英,&康雪雅.(2007).LiAl0.03Mn1.97O4的流变相辅助微波合成及电化学性能.电子元件与材料,26(12),10-13. |
MLA | 崔涛,et al."LiAl0.03Mn1.97O4的流变相辅助微波合成及电化学性能".电子元件与材料 26.12(2007):10-13. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论