中文摘要	采用传统固相法制备了Co1.5 xMn1.2Ni0.3AlxO4(x=0,0.02,0.04,0.06)NTC热敏电阻材料。借助XRD、SEM和几种电性能测试手段,研究了Al2O3掺杂对MnCoNi热敏电阻材料相结构及电性能的影响。结果表明:随着Al2O3掺杂量的增加,MnCoNi热敏电阻材料的晶体结构不变,晶粒减小,电阻率和材料常数B值由339.07Ω·cm、3489.07K分别增加到3723.89Ω·cm、3956.80K,电学稳定性由1.65%提高至0.17%。
英文摘要	Co_(1.5-x)Mn_(1.2)Ni_(0.3)Al_xO_4(x=0,0.02,0.04,0.06)NTC thermistor materials were prepared by the traditional solid-state reaction method.The effects of Al_2O_3 doping on the microstructure and electric properties of prepared materials were studied through XRD,SEM and several instruments for electrical properties characterization.The results indicate that Al_2O_3 doping shows little effect on the crystal structure of prepared materials.However,with increasing Al_2O_3 content,the grain size of the MnCoNi thermistor materials decreases,while the resistivity,material constant B value and electrical stability increase from 339.07Omega·cm,3 489.07 K and 1.65%to 3 723.89Omega·cm,3 956.80 K and 0.17%,respectively.
学科主题	Engineering (provided by Thomson Reuters)
公开日期	2012-11-29
内容类型	期刊论文
源URL	[http://ir.xjipc.cas.cn/handle/365002/1573]
专题	新疆理化技术研究所_新疆维吾尔自治区电子信息材料与器件重点实验室新疆理化技术研究所_材料物理与化学研究室
作者单位	中国科学院新疆理化技术研究所；新疆电子信息材料与器件重点实验室;中国科学院研究生院
推荐引用方式 GB/T 7714	黄霞,姚金城,常爱民,等. Al2O3掺杂对MnCoNi系NTC热敏电阻材料性能的影响[J]. 电子元件与材料,2011,30(7):25-28.
APA	黄霞,姚金城,常爱民,刘力,&彭昌文.(2011).Al2O3掺杂对MnCoNi系NTC热敏电阻材料性能的影响.电子元件与材料,30(7),25-28.
MLA	黄霞,et al."Al2O3掺杂对MnCoNi系NTC热敏电阻材料性能的影响".电子元件与材料 30.7(2011):25-28.