非线性光学晶体Ba2B5O9Cl的合成、晶体生长及性能的研究 | |
陈兆慧; 潘世烈![]() ![]() ![]() | |
刊名 | 人工晶体学报
![]() |
2011 | |
卷号 | 40期号:6页码:1394-1398 |
关键词 | Barium Crystal growth Crystal structure Fluxes Spectroscopy |
ISSN号 | 1000-985X |
其他题名 | study on synthesis, crystal growth and properties of nonlinear optical crystal ba2b5o9cl |
中文摘要 | 首次以LiF-H3BO3为助熔剂,用顶部籽晶法,生长出尺寸为12 mm×13mm×5mm的Ba2B5O9Cl透明单晶.通过热性能分析证实该晶体为非同成分熔融化合物,属于正交晶系,空间群Pnn2,晶胞参数为a=1.1576(2) nm,b=1.1619(2)nm,c =0.66874(13) nm,V=0.8994(3) nm3,Z=4.该晶体中含有BO3和BO3基团,具有三维网状的晶体结构.Ba2B5O9Cl粉末的非线性光学效应约为KDP的3.5倍,同时还进行了红外、漫反射光谱性能的研究. |
英文摘要 | Single crystals of Ba2B5O9Cl with sizes up to 12 mm × 13 mm × 5 mm have been grown by top seeded solution growth method using LiF-H3BO3 as the flux for the first time. The TGA-DSC experiments proved that Ba2B5O9Cl melts incongruently. It crystallizes in the orthorhombic system, space group Pnn2, with unit-cell parameters a=1.1576(2) nm, b=1.1619(2) nm, c=0.66874(13) nm, V=0.8994(3) nm3, Z=4.There are BO3 and BO4 groups in the Ba2B5O9Cl crystal and it exhibits a three-dimensional network structure. Nonlinear optical efficiency of Ba2B5O9Cl is about 3.5 times that of KDP. The infrared spectrum and the UV-Vis diffuse reflectance spectroscopy were also performed on the reported material. |
公开日期 | 2012-11-29 |
内容类型 | 期刊论文 |
源URL | [http://ir.xjipc.cas.cn/handle/365002/1447] ![]() |
专题 | 新疆理化技术研究所_新疆维吾尔自治区电子信息材料与器件重点实验室 新疆理化技术研究所_材料物理与化学研究室 |
作者单位 | 中国科学院新疆理化技术研究所;新疆电子信息材料与器件重点实验室;中国科学院研究生院;新疆大学理化测试中心 |
推荐引用方式 GB/T 7714 | 陈兆慧,潘世烈,赵文武,等. 非线性光学晶体Ba2B5O9Cl的合成、晶体生长及性能的研究[J]. 人工晶体学报,2011,40(6):1394-1398. |
APA | 陈兆慧,潘世烈,赵文武,杨云,吴红萍,&张方方.(2011).非线性光学晶体Ba2B5O9Cl的合成、晶体生长及性能的研究.人工晶体学报,40(6),1394-1398. |
MLA | 陈兆慧,et al."非线性光学晶体Ba2B5O9Cl的合成、晶体生长及性能的研究".人工晶体学报 40.6(2011):1394-1398. |