Ultralow friction behaviors of hydrogenated fullerene-like carbon films: effect of normal load and surface tribochemistry | |
Zhang JY(张俊彦)![]() ![]() ![]() | |
刊名 | Tribology Letters
![]() |
2011 | |
卷号 | 41页码:607-615 |
关键词 | Hydrogenated fullerene-like carbon Ultralow friction Elasticity Tribochemistry |
ISSN号 | 1023-8883 |
通讯作者 | 张俊彦 |
中文摘要 | Friction and wear behaviors of hydrogenated fullerene-like (H-FLC) carbon films sliding against Si3N4 ceramic balls were performed at different contact loads from 1 to 20 N on a reciprocating sliding tribometer in air. It was found that the films exhibited non-Amontonian friction behaviors, the coefficient of friction (COF) decreased with normal contact load increasingthe COF was *0.112 at 1 N contact load, and deceased to ultralow value (*0.009) at 20 N load. The main mechanism responsible for low friction and wear under varying contact pressure is governed by hydrogenated carbon transfer film that formed and resided at the sliding interfaces. In addi- tion, the unique fullerene-like structures induce well elastic property of the H-FLC films (elastic recovery 78%), which benefits the high load tolerance and induces the low wear rate in air condition. For the film with an ultralow COF of 0.009 tested under 20 N load in air, time of flight sec- ondary ion mass spectrometry (ToF-SIMS) signals col- lected inside and outside the wear tracks indicated the presence of C2H3 - and C2H5 - fragments after tribological tests on the H-FLC films surface. We think that the tribo- chemistry and elastic property of the H-FLC films is responsible for the observed friction behaviors, the high load tolerance, and chemical inertness of hydrogenated carbon-containing transfer films instead of the graphitization of transfer films is responsible for the steady-state low coefficients of friction, wear, and interfacial shear stress. |
学科主题 | 材料科学与物理化学 |
收录类别 | SCI |
资助信息 | the National Natural Science Foundation of China (Grant nos. 50572108,50975273,50721062,51005110) |
语种 | 英语 |
WOS记录号 | WOS:000287498400014 |
公开日期 | 2012-09-24 |
内容类型 | 期刊论文 |
源URL | [http://210.77.64.217/handle/362003/862] ![]() |
专题 | 兰州化学物理研究所_固体润滑国家重点实验室 |
通讯作者 | Zhang JY(张俊彦); Zhang JY(张俊彦) |
推荐引用方式 GB/T 7714 | Zhang JY,Zhang JY,Zhang B. Ultralow friction behaviors of hydrogenated fullerene-like carbon films: effect of normal load and surface tribochemistry[J]. Tribology Letters,2011,41:607-615. |
APA | 张俊彦,张俊彦,&张斌.(2011).Ultralow friction behaviors of hydrogenated fullerene-like carbon films: effect of normal load and surface tribochemistry.Tribology Letters,41,607-615. |
MLA | 张俊彦,et al."Ultralow friction behaviors of hydrogenated fullerene-like carbon films: effect of normal load and surface tribochemistry".Tribology Letters 41(2011):607-615. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论