Tribocorrosion behaviour of Ni–17.5Si–29.3Cr alloy in sulfuric acid solution | |
Ma JQ(马吉强); Liu WM(刘维民); Xue QJ(薛群基); Yang J(杨军); Bi QL(毕秦岭); Bi QL(毕秦岭) | |
刊名 | Tribology International |
2009 | |
卷号 | 42页码:1081-1087 |
关键词 | Ni-17.5Si-29.3Cr alloy Tribocorrosion H2SO4 Wear |
ISSN号 | 0301-679X |
通讯作者 | 毕秦岭 |
中文摘要 | The tribocorrosion property of a Ni-17.5Si-29.3Cr alloy against a Si3N4 ball was studied in comparison with AISI321 stainless steel using a ball-on-disk reciprocating tribotester in 1M sulfuric acid (H2SO4) solution. The effects of load and sliding speed on the tribocorrosion properties of the alloy were investigated. The results indicated that the wear rate of the alloy increased while the friction coefficient decreased with increasing load. The wear rate of the alloy increased linearly with increasing sliding speed and the friction coefficient increased in the initial stages and then remained constant with increasing sliding speed. The wear mechanisms were mainly microploughing, uniform corrosion and pitting corrosion. Under the experimental conditions of the present study, the Ni-17.5Si-29.3Cr alloy showed excellent corrosion-resistence and anti-wear ability compared with AISI321 stainless steel. |
学科主题 | 材料科学与物理化学 |
收录类别 | SCI |
资助信息 | the National Natural Science Foundation of China (50845063);the National 973 Project (2007CB607601) |
语种 | 英语 |
公开日期 | 2012-11-13 |
内容类型 | 期刊论文 |
源URL | [http://210.77.64.217/handle/362003/2136] |
专题 | 兰州化学物理研究所_固体润滑国家重点实验室 |
通讯作者 | Bi QL(毕秦岭); Bi QL(毕秦岭) |
推荐引用方式 GB/T 7714 | Ma JQ,Liu WM,Xue QJ,et al. Tribocorrosion behaviour of Ni–17.5Si–29.3Cr alloy in sulfuric acid solution[J]. Tribology International,2009,42:1081-1087. |
APA | 马吉强,刘维民,薛群基,杨军,毕秦岭,&毕秦岭.(2009).Tribocorrosion behaviour of Ni–17.5Si–29.3Cr alloy in sulfuric acid solution.Tribology International,42,1081-1087. |
MLA | 马吉强,et al."Tribocorrosion behaviour of Ni–17.5Si–29.3Cr alloy in sulfuric acid solution".Tribology International 42(2009):1081-1087. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论