CeO2-MOX (M=La3+, Ca2+)改性Pd/g-Al2O3催化甲烷燃烧性能 | |
孙鲲鹏![]() | |
刊名 | 物理化学学报
![]() |
2008 | |
卷号 | 24期号:11页码:2108-2113 |
关键词 | CeO2-MOx solid solution Pd/γ-Al2O3 catalyst Catalytic methane combustion XRD Raman XPS CeO2-MOx固溶体 Pd/γ-Al2O3催化剂 甲烷催化燃烧 |
ISSN号 | 1000-6818 |
通讯作者 | 肖利华 |
中文摘要 | Solid solution CeO2-MOx (M=La3+, Ca2+) promoted Pd/γ-Al2O3 catalysts were prepared by a depositionprecipitation method. The structural properties were investigated by X-ray diffraction, X-ray photoelectron spectroscopy, and Raman spectroscopy. The results showed that Mn+ ions incorporated into CeO2 lattice and solid solutions formed in Pd/γ-Al2O3-CeO2-MOx catalysts. The formation of solid solution was confirmed by the change in lattice parameters of CeO2 and the shift of 2θ angles as compared with pure CeO2. A strain formed in the O2- sub-lattice of CeO2 was revealed by Raman analyses, which decreased the intensity of the Raman-active band at around 463 cm-1 owing to the F2g symmetric stretching of Ce—O bond. The appearance of a new band at 615 cm-1 (in the case of Pd/γ-Al2O3-CeO2-CaO) and a shoulder at 320 cm-1 (in the case of Pd/γ-Al2O3-CeO2-La2O3) was also confirmed. Ionic Pdδ+ species were formed in the catalysts, which exhibited higher binding energies (0.5-0.6 eV higher for Pd 3d5/2) than that of normal PdO. The catalysts showed high activity and stability for low temperature methane combustion. 10% and 100% conversions of methane could be obtained at temperatures of 254 and 340 ℃, respectively, over Pd/γ-Al2O3-CeO2-La2O3 catalyst under an hourly space velocity of 50000 h-1. |
学科主题 | 物理化学 |
收录类别 | CSCD |
语种 | 英语 |
公开日期 | 2012-11-09 |
内容类型 | 期刊论文 |
源URL | [http://210.77.64.217/handle/362003/1975] ![]() |
专题 | 兰州化学物理研究所_OSSO国家重点实验室 兰州化学物理研究所_绿色化学研究发展中心 |
推荐引用方式 GB/T 7714 | 孙鲲鹏. CeO2-MOX (M=La3+, Ca2+)改性Pd/g-Al2O3催化甲烷燃烧性能[J]. 物理化学学报,2008,24(11):2108-2113. |
APA | 孙鲲鹏.(2008).CeO2-MOX (M=La3+, Ca2+)改性Pd/g-Al2O3催化甲烷燃烧性能.物理化学学报,24(11),2108-2113. |
MLA | 孙鲲鹏."CeO2-MOX (M=La3+, Ca2+)改性Pd/g-Al2O3催化甲烷燃烧性能".物理化学学报 24.11(2008):2108-2113. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论