Analysis of cavity evolution in 9%Cr heat-resistant steel welded joint during creep | |
Wang, Xue; Wang, Xiao; Luo, Bin; Guo, Jialin | |
刊名 | ENGINEERING FRACTURE MECHANICS
![]() |
2018 | |
卷号 | 202 |
关键词 | 9%Cr heat-resistant steel Welded joints Creep void Creep failure |
ISSN号 | 0013-7944 |
DOI | 10.1016/j.engfracmech.2018.08.006 |
URL标识 | 查看原文 |
收录类别 | SCIE ; EI |
语种 | 英语 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/4238540 |
专题 | 武汉大学 |
推荐引用方式 GB/T 7714 | Wang, Xue,Wang, Xiao,Luo, Bin,et al. Analysis of cavity evolution in 9%Cr heat-resistant steel welded joint during creep[J]. ENGINEERING FRACTURE MECHANICS,2018,202. |
APA | Wang, Xue,Wang, Xiao,Luo, Bin,&Guo, Jialin.(2018).Analysis of cavity evolution in 9%Cr heat-resistant steel welded joint during creep.ENGINEERING FRACTURE MECHANICS,202. |
MLA | Wang, Xue,et al."Analysis of cavity evolution in 9%Cr heat-resistant steel welded joint during creep".ENGINEERING FRACTURE MECHANICS 202(2018). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论