Synthesis and stabilization of high-molecular-weight poly(propylene carbonate) from Zn-Co-based double metal cyanide catalyst | |
Li ZF ; Qin YS ; Zhao XJ ; Wang FS ; Zhang SB ; Wang XH | |
刊名 | european polymer journal |
2011 | |
卷号 | 47期号:11页码:2152-2157 |
关键词 | DIIMINATE ZINC CATALYSTS DIHYDRIC PHENOL SYSTEM PROPYLENE-OXIDE ALTERNATING COPOLYMERIZATION CO2/EPOXIDE COPOLYMERIZATION POLYCARBONATE SYNTHESIS COORDINATION CATALYST LIVING POLYMERIZATION CHEMISTRY RELEVANT ALUMINUM PORPHYRIN |
ISSN号 | 0014-3057 |
通讯作者 | wang xh |
中文摘要 | high-molecular-weight poly(propylene carbonate) (ppc) was synthesized using a zn-co-based double metal cyanide (co-dmc) catalyst. the catalytic activity reached as high as 60.6 kg polymer/g co-dmc after 10 h when the low-molecular-weight polyether polyol initiator was not used. in contrast, production of the by-product propylene carbonate (pc) significantly decreased to below 1.0 wt%. considering the carbonate content in the alternative copolymer as 100%, the carbonate content of the obtained ppc ranged between 34% and 49%. the carbonate content was highly important for the air stability of ppc. the number average molecular weight of the as-polymerized ppc with a carbonate content of 48% reached 130 kg/mol. however, it decreased to ca. 60 kg/mol after 24 h of storage at 70 c, and further dropped to ca. 40 kg/mol after 7 d. this result confirmed that severe oxidative degradation occurred for the low-carbonate-content ppc. air stability significantly improved by adding antioxidant 1010 (tetrakisl methylene(3,5-di-(tert-butyl)-4-hydroxy-hydro cinnamate)] methane). similarly, a more air stable ppc was also prepared by raising its carbonate content. our work provided a new explanation on the wide existence of low-molecular-weight ppc in dmc catalyst literature. strategies for obtaining high-molecular-weight ppc were also disclosed. (c) 2011 elsevier ltd. all rights reserved. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000297449600012 |
公开日期 | 2012-06-08 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/44249] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Li ZF,Qin YS,Zhao XJ,et al. Synthesis and stabilization of high-molecular-weight poly(propylene carbonate) from Zn-Co-based double metal cyanide catalyst[J]. european polymer journal,2011,47(11):2152-2157. |
APA | Li ZF,Qin YS,Zhao XJ,Wang FS,Zhang SB,&Wang XH.(2011).Synthesis and stabilization of high-molecular-weight poly(propylene carbonate) from Zn-Co-based double metal cyanide catalyst.european polymer journal,47(11),2152-2157. |
MLA | Li ZF,et al."Synthesis and stabilization of high-molecular-weight poly(propylene carbonate) from Zn-Co-based double metal cyanide catalyst".european polymer journal 47.11(2011):2152-2157. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论