Microstructural and magnetic characteristics of nanocrystalline Fe89Zr7B4 soft magnetic alloys | |
F. Zhou ; K. Y. He ; K. C. Bai | |
刊名 | Journal of Applied Physics |
1996 | |
卷号 | 80期号:9页码:5209-5212 |
关键词 | fe-zr-b high saturation magnetization nanoscale grain-size core losses nb alloys fe73.5cu1nb3si13.5b9 ferromagnets dependence hf |
ISSN号 | 0021-8979 |
中文摘要 | Nanocrystalline (NC) Fe89Zr7B4 soft magnetic alloys, consisting of an alpha-Fe crystalline phase and a residual amorphous phase, were synthesized by crystallizing the original amorphous samples at temperatures between 773 and 923 K. Microstructure of the alloys was characterized by x-ray diffraction and Mossbauer spectroscopy. Few of solute atoms was found in the alpha-Fe phase precipitated at various temperatures. The volume fractions of the residual amorphous phase in the alloys are in the range of 334b-36%. Moreover, the difference in values for the intensity of the specific saturation magnetization between the residual amorphous phase and the alpha-Fe phase, evaluated by the Mossbauer spectroscopy and the magnetic analysis technique, is considerably large, which might be mainly responsible for the relatively lower permeability of the NC Fe89Zr7B4 alloys than of the NC Fe73.5Cu1Nb3Si13.5B9 alloy. (C) 1996 American Institute of Physics. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/38513] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | F. Zhou,K. Y. He,K. C. Bai. Microstructural and magnetic characteristics of nanocrystalline Fe89Zr7B4 soft magnetic alloys[J]. Journal of Applied Physics,1996,80(9):5209-5212. |
APA | F. Zhou,K. Y. He,&K. C. Bai.(1996).Microstructural and magnetic characteristics of nanocrystalline Fe89Zr7B4 soft magnetic alloys.Journal of Applied Physics,80(9),5209-5212. |
MLA | F. Zhou,et al."Microstructural and magnetic characteristics of nanocrystalline Fe89Zr7B4 soft magnetic alloys".Journal of Applied Physics 80.9(1996):5209-5212. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论