Erosion behaviour of TiNi alloy foils under various heat treatments

CORC > 金属研究所 > 中国科学院金属研究所

	Erosion behaviour of TiNi alloy foils under various heat treatments
	Y. N. Liang ; Z. C. Wang ; S. Z. Li ; Z. Y. Si
刊名	Journal of Materials Science & Technology
	1996
卷号	12 期号:4 页码:286-290
关键词	memory
ISSN号	1005-0302
中文摘要	The erosion behaviour of TiNi alloy foils (Ni: 50.5 at pct, thickness: 70-90 mu m) under various heat treatments has been studied with two different tests: sand-blasting erosion (SBE) with impingement angle of 30 degrees and slurry erosion (SE). The erosion resistance of the foils aged at 400-450 degrees C/30 min is the best in all tests. The quenched foil is also good in the SBE test, but not so good in the SE test. The slurry-erosion resistance of the aged foils is better than that of L214 with high hardness. All the foils exhibit much better erosion resistance than 18Cr-8Ni stainless steel in the tests.
原文出处	://WOS:A1996UW20000009
公开日期	2012-04-14
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/38335]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Y. N. Liang,Z. C. Wang,S. Z. Li,et al. Erosion behaviour of TiNi alloy foils under various heat treatments[J]. Journal of Materials Science & Technology,1996,12(4):286-290.
APA	Y. N. Liang,Z. C. Wang,S. Z. Li,&Z. Y. Si.(1996).Erosion behaviour of TiNi alloy foils under various heat treatments.Journal of Materials Science & Technology,12(4),286-290.
MLA	Y. N. Liang,et al."Erosion behaviour of TiNi alloy foils under various heat treatments".Journal of Materials Science & Technology 12.4(1996):286-290.