Effect of solidification rate on the microstructure of a Ni-base superalloy | |
X. B. Huang ; Y. Zhang ; Z. Q. Hu ; H. H. Deng ; Y. L. Liu | |
刊名 | Materials Transactions Jim |
1997 | |
卷号 | 38期号:11页码:1016-1021 |
关键词 | superalloy solidification microstructure |
ISSN号 | 0916-1821 |
中文摘要 | The effect of solidification rate on the solidified structure, solute segregation and microstructures such as carbide, gamma'gamma eutectic, gamma' phase and dendrite arm spacing was experimentally investigated employing a method of partially directional solidification and subsequent quick quenching. Three types of the solidified structure were identified: cellular, cellular-dendritic and developed dendrite-type, and the width of a mushy zone was narrowed when solidification rate increased from 2.5 mu m/s to 125 mu m/s. The carbide morphologies were affected by both solidified structure and solidification rate, it formed into bar-type in the cellular structure, and Chinese script-type in the dendrite structure. The increase of solidification rate caused a lot of gamma'/gamma eutectic and the change of gamma' phase from cubic into cubic-round. The dendrite arm spacing decreased and the segregation of Cr, Al, Co, Mo, Ti was alleviated with increasing solidification rate. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/37981] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | X. B. Huang,Y. Zhang,Z. Q. Hu,et al. Effect of solidification rate on the microstructure of a Ni-base superalloy[J]. Materials Transactions Jim,1997,38(11):1016-1021. |
APA | X. B. Huang,Y. Zhang,Z. Q. Hu,H. H. Deng,&Y. L. Liu.(1997).Effect of solidification rate on the microstructure of a Ni-base superalloy.Materials Transactions Jim,38(11),1016-1021. |
MLA | X. B. Huang,et al."Effect of solidification rate on the microstructure of a Ni-base superalloy".Materials Transactions Jim 38.11(1997):1016-1021. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论