Oxidation of gamma-TiAl intermetallic coated with electrodeposited nickel-La2O3 composite films | |
X. Peng ; Z. Tang ; T. Li ; W. Wu | |
刊名 | Oxidation of Metals |
1999 | |
卷号 | 51期号:3-4页码:317-331 |
关键词 | oxidation gamma-TiAl intermetallic electrodeposited Ni-La2O3 composite film behavior alloys |
ISSN号 | 0030-770X |
中文摘要 | A coating of nickel with La2O3 particles was electrodeposited on the surface of gamma-TiAl to improve its high-temperature oxidation resistance. The experimental results showed that contrary to the oxidation of bare specimens, the electrodeposited Ni-La2O3 composite-coated ones exhibited much better resistance to both isothermal and cyclic oxidation in air at 1000 and 900 degrees C. For the oxidation of the Ni-La2O3 composite-coated gamma-TiAl EPMA/EDX microanalyses revealed that after the composite film had been thoroughly oxidized, a La2O3-rich NiO layer close to the gas-scale interface and two alumina-rich layers, with one beneath the NiO layer and the other adjacent to the gamma-TiAl matrix, were produced in the scale. The results indicated that the preferentially formed La2O3-doped NiO layer retarded the growth of rutile and favor ed the formation of two alumina-rich layers. The mechanism of the effect of the electrodeposited Ni-La2O3 composite on the oxidation behavior of gamma-TiAl is discussed in detail. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/37472] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | X. Peng,Z. Tang,T. Li,et al. Oxidation of gamma-TiAl intermetallic coated with electrodeposited nickel-La2O3 composite films[J]. Oxidation of Metals,1999,51(3-4):317-331. |
APA | X. Peng,Z. Tang,T. Li,&W. Wu.(1999).Oxidation of gamma-TiAl intermetallic coated with electrodeposited nickel-La2O3 composite films.Oxidation of Metals,51(3-4),317-331. |
MLA | X. Peng,et al."Oxidation of gamma-TiAl intermetallic coated with electrodeposited nickel-La2O3 composite films".Oxidation of Metals 51.3-4(1999):317-331. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论