Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air

CORC > 金属研究所 > 中国科学院金属研究所

	Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air
	P. S. Liu ; K. M. Liang ; S. R. Gu
刊名	Oxidation of Metals
	2000
卷号	54 期号:3-4 页码:277-283
关键词	aluminide coating Co-base superalloy high-temperature oxidation corrosion nodule
ISSN号	0030-770X
中文摘要	A surface-morphology change has been observed for an aluminide coating on the Go-base superalloy DZ40M during oxidation at 1100 degrees C in air. The oxide formed on the coating remained an even greyish-white color during the stable oxidation stage, whereas, dark-colored corrosion nodules were observed when oxidation of the coating accelerated. The number of nodules increased with time, along with growth of the nodules, eventually covering the entire surface which signified failure.
原文出处	://WOS:000088799600005
公开日期	2012-04-14
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/37102]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	P. S. Liu,K. M. Liang,S. R. Gu. Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air[J]. Oxidation of Metals,2000,54(3-4):277-283.
APA	P. S. Liu,K. M. Liang,&S. R. Gu.(2000).Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air.Oxidation of Metals,54(3-4),277-283.
MLA	P. S. Liu,et al."Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air".Oxidation of Metals 54.3-4(2000):277-283.