High-pressure synthesis and properties of CeO2-ZrO2 solid solution | |
D. P. Xu ; Q. Y. Wang ; Z. Lu ; Z. G. Liu ; G. M. Zhang ; W. H. Su | |
刊名 | Chinese Science Bulletin
![]() |
2001 | |
卷号 | 46期号:10页码:801-806 |
关键词 | CeO2-ZrO2 nanocrystalline high pressure and -temperature solid-state reaction solid solution hydrothermal synthesis electrical-properties nanocrystalline stability system |
ISSN号 | 1001-6538 |
中文摘要 | Using nanoparticles of CeO2 and ZrO2 prepared by the chemical precipitation method as starting materials, the single-phase cubic Ce0.5Zr0.5O2 solid solution (c-Ce0.5Zr0.5O2) has been synthesized under 3.1 GPa at 1073 K for the first time. The structure of the c-Ce0.5Zr0.5O2 has not been changed before and after annealing at 773 K for 1 h. Only an unknown EPR signal (g = 1.990) has been observed in the c-Ce0.5Zr0.5O2 and not varied after annealing at 773 K for 1 h, which exhibited that there exists no Ce3+ in the c-Ce0.5Zr0.5O2 and the Ce4+ has not been reduced into Ce3+ after annealing. The transport mechanism is ionic for the c-Ce0.5Zr0.5O2. The bulk conductivity (sigma =1.2 x 10(-5) S/cm at 823 K, sigma = 2.1 x 10(-3) S/cm at 1123 K) is the same as that of CeO2, but smaller than that of Y2O3-stabilized ZrO2. A marked curvature at T = 823 K has been observed in the Arrhenius plot of the bulk conductivity. The activation energy below 823 K is lower than that above 823 K, and the reason has been discussed. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/36853] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | D. P. Xu,Q. Y. Wang,Z. Lu,et al. High-pressure synthesis and properties of CeO2-ZrO2 solid solution[J]. Chinese Science Bulletin,2001,46(10):801-806. |
APA | D. P. Xu,Q. Y. Wang,Z. Lu,Z. G. Liu,G. M. Zhang,&W. H. Su.(2001).High-pressure synthesis and properties of CeO2-ZrO2 solid solution.Chinese Science Bulletin,46(10),801-806. |
MLA | D. P. Xu,et al."High-pressure synthesis and properties of CeO2-ZrO2 solid solution".Chinese Science Bulletin 46.10(2001):801-806. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论