Preparation and electrorheological characteristics of rare-earth-doped TiO2 suspensions | |
X. P. Zhao ; J. B. Yin | |
刊名 | Chemistry of Materials
![]() |
2002 | |
卷号 | 14期号:5页码:2258-2263 |
关键词 | fluids dependence |
ISSN号 | 0897-4756 |
中文摘要 | According to the dielectric design, a new kind of rare-earth (RE)-doped TiO2 particle was synthesized by means of sol-gel technique for use in electrorheological (ER) fluids. A distinct enhancement in the yield stress under dc electric field was found by using such particles, when compared with that of pure TiO2. The yield stress of typical cerium-doped TiO2 suspension was about 5.0 kPa at 3 kV/mm and 7.0 kPa at 4 kV/mm, which were 10 times higher than that of a pure TiO2 suspension. The yield stress showed a marked dependence on RE-doping degree. Substitution of 10 mol % cerium or 8 mol % lanthanum for Ti could obtain the highest yield stress. These were well explained by the dielectric measurements that showed an increase in the dielectric loss and the dielectric constant at low frequency and their regular change with rare earth content. The lattice distortion and defects in the TiO2 crystal caused by substitution for Ti with large-radius RE ions may be responsible for the obvious improvement noted above. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/36570] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | X. P. Zhao,J. B. Yin. Preparation and electrorheological characteristics of rare-earth-doped TiO2 suspensions[J]. Chemistry of Materials,2002,14(5):2258-2263. |
APA | X. P. Zhao,&J. B. Yin.(2002).Preparation and electrorheological characteristics of rare-earth-doped TiO2 suspensions.Chemistry of Materials,14(5),2258-2263. |
MLA | X. P. Zhao,et al."Preparation and electrorheological characteristics of rare-earth-doped TiO2 suspensions".Chemistry of Materials 14.5(2002):2258-2263. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论