Improving the oxidation resistance of Ti3SiC2 by forming a Ti3Si0.9Al0.1C2 solid solution | |
H. B. Zhang ; Y. C. Zhou ; Y. W. Bao ; M. S. Li | |
刊名 | Acta Materialia
![]() |
2004 | |
卷号 | 52期号:12页码:3631-3637 |
关键词 | ceramics oxidation layered structures activity solid solution high-temperature mechanical-properties silicon-nitride si3n4-tin composites behavior air ceramics ti3alc2 powders si |
ISSN号 | 1359-6454 |
中文摘要 | The oxidation behavior of the Ti3Si0.9Al0.1C2 solid solution in air was investigated at 1000-1350 degreesC. The parabolic rate constants of Ti3Si0.9Al0.1C2 were decreased by 2-4 orders of magnitude compared with those of Ti3SiC2 at 1000-1300 degreesC. At 1000-1100 degreesC, the oxide scales displayed a continuous alpha-Al-2-O-3 inner layer and a discontinuous TiO2 (rutile) outer layer. At 1200-1300 degreesC, the continuous inner layer was still alpha-Al2O3, but the outer layer was a mixture of TiO2 (rutile) and Al2TiO5. The oxide layers were dense, adherent and resistant to thermal cycling. However, the oxidation resistance of Ti3Si0.9Al0.1C2 deteriorated at 1350 degreesC because of the depletion of alpha-Al2O3. This depletion was caused by the extensive reaction between TiO2 (rutile) and alpha-Al2O3 to form Al2TiO5. The high activity and diffusion of Al and the low solubility of oxygen in the solid solution were the key factors for the formation of a continuous alpha-Al2O3 layer during high-temperature oxidation. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/35708] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | H. B. Zhang,Y. C. Zhou,Y. W. Bao,et al. Improving the oxidation resistance of Ti3SiC2 by forming a Ti3Si0.9Al0.1C2 solid solution[J]. Acta Materialia,2004,52(12):3631-3637. |
APA | H. B. Zhang,Y. C. Zhou,Y. W. Bao,&M. S. Li.(2004).Improving the oxidation resistance of Ti3SiC2 by forming a Ti3Si0.9Al0.1C2 solid solution.Acta Materialia,52(12),3631-3637. |
MLA | H. B. Zhang,et al."Improving the oxidation resistance of Ti3SiC2 by forming a Ti3Si0.9Al0.1C2 solid solution".Acta Materialia 52.12(2004):3631-3637. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论