Superplasticity in a directionally solidiried multiphase Ni-25Al-25Cr alloy | |
J. T. Guo ; J. Zhou | |
刊名 | Zeitschrift Fur Metallkunde
![]() |
2004 | |
卷号 | 95期号:1页码:22-26 |
关键词 | NiAl superplastic behavior casting microstructure internal-stress superplasticity polycrystalline materials large grains transformation deformation microstructure intermetallics mechanism creep iron |
ISSN号 | 0044-3093 |
中文摘要 | A Ni-25Al-25Cr (at.%) alloy was directionally solidified under Ar atmosphere in an A1(2)O(3)-SiO2 ceramic mold by the standard Bridgman method. The microstructure of the as-fabricated alloy was studied using optical microscopy, X-ray diffraction and scanning electron microscopy. The alloy was composed of beta-NiAl dendritic arms, alpha-Cr interdendritic regions, fine alpha-Cr particles in the dendritic arms, and beta-NiAl + alpha-Cr eutectic in the interdendritic regions. The mechanical properties were studied by tensile tests in the temperature range 1123 - 1373 K. The results showed that the alloy exhibits superplastic behavior at appropriate testing conditions. The balance between work hardening (by dislocation glide) and work softening (by dynamic recovery and recrystallization) is responsible for the large tensile elongation of the alloy. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/35366] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | J. T. Guo,J. Zhou. Superplasticity in a directionally solidiried multiphase Ni-25Al-25Cr alloy[J]. Zeitschrift Fur Metallkunde,2004,95(1):22-26. |
APA | J. T. Guo,&J. Zhou.(2004).Superplasticity in a directionally solidiried multiphase Ni-25Al-25Cr alloy.Zeitschrift Fur Metallkunde,95(1),22-26. |
MLA | J. T. Guo,et al."Superplasticity in a directionally solidiried multiphase Ni-25Al-25Cr alloy".Zeitschrift Fur Metallkunde 95.1(2004):22-26. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论