A screen-printed Ce0.8Sm0.2O1.9 film solid oxide fuel cell with a Ba0.5Sr0.5Co0.8Fe0.2O3-delta cathode | |
Y. H. Zhang ; X. Q. Huang ; Z. Lu ; Z. G. Liu ; X. D. Ge ; J. H. Xu ; X. S. Xin ; X. Q. Sha ; W. H. Su | |
刊名 | Journal of Power Sources |
2006 | |
卷号 | 160期号:2页码:1217-1220 |
关键词 | solid oxide fuel cells screen-printing electrolyte films Ce0.8Sm0.2O1.9 Ba0.5Sr0.5Co0.8Fe0.2O3-delta thin-film temperature sofcs electrolyte performance |
ISSN号 | 0378-7753 |
中文摘要 | Screen-printing technology was developed to fabricate Ce0.8Sm0.2O1.9 (SDC) electrolyte films onto porous NiO-SDC green anode substrates. After sintering at 1400 degrees C for 4 h, a gas-tight SDC film with a thickness of 12 mu m was obtained. A novel cathode material of Ba0.5Sr0.5Co0.8Fe0.2O3-delta Was subsequently applied onto the sintered SDC electrolyte film also by screen-printing and sintered at 970 degrees C for 3 h to get a single cell. A fuel cell of Ni-SDC/SDC (12 mu m)/Ba0.5Sr0.5Co0.8Fe0.2O3-delta provides the maximum power densities of 1280, 1080, 670, 370, 180 and 73 mW cm(-2) at 650, 600, 555, 505, 455 and 405 degrees C, respectively, using hydrogen as fuel and stationary air as oxidant. When dry methane was used as fuel, the maximum power densities are 876, 568, 346 and 114 mW cm(-2) at 650, 600, 555 and 505 degrees C, respectively. ne present fuel cell shows excellent performance at lowered temperatures. (c) 2006 Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/34724] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Y. H. Zhang,X. Q. Huang,Z. Lu,et al. A screen-printed Ce0.8Sm0.2O1.9 film solid oxide fuel cell with a Ba0.5Sr0.5Co0.8Fe0.2O3-delta cathode[J]. Journal of Power Sources,2006,160(2):1217-1220. |
APA | Y. H. Zhang.,X. Q. Huang.,Z. Lu.,Z. G. Liu.,X. D. Ge.,...&W. H. Su.(2006).A screen-printed Ce0.8Sm0.2O1.9 film solid oxide fuel cell with a Ba0.5Sr0.5Co0.8Fe0.2O3-delta cathode.Journal of Power Sources,160(2),1217-1220. |
MLA | Y. H. Zhang,et al."A screen-printed Ce0.8Sm0.2O1.9 film solid oxide fuel cell with a Ba0.5Sr0.5Co0.8Fe0.2O3-delta cathode".Journal of Power Sources 160.2(2006):1217-1220. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论