Intermediate phases in synthesis of Ti3SiC2 and Ti3Si(Al)C-2 solid solutions from elemental powders | |
H. B. Zhang ; Y. C. Zhou ; Y. W. Bao ; M. S. Li ; J. Y. Wang | |
刊名 | Journal of the European Ceramic Society |
2006 | |
卷号 | 26期号:12页码:2373-2380 |
关键词 | Ti3SiC2 hot pressing impurities X-ray methods high-temperature synthesis titanium-silicon carbide si-c system oxidation resistance combustion synthesis neutron-diffraction reaction-mechanism rapid synthesis growth carbon |
ISSN号 | 0955-2219 |
中文摘要 | In this paper. we investigated the reaction path to synthesize Ti3SiC2 by the in situ hot pressing/solid-liquid reaction method. The effect of different content of Al addition on this process was also examined. Ti3SiC2 mainly formed from the reaction between Ti5Si3C(x), TiCx, TiSi2 and graphite at 1400-1500 degrees C. As an inescapable impurity in Ti3SiC2, TiCx was removed by addition of small amounts of Al. This was owing to the fact that the addition of a minor quantity of Al increased the amount of "effective TiCx" and relatively decreased that of "invalid TiCx". Further increasing Al content. however, resulted in the presence of TiCx again in the final product. This was due to the fact when significant amounts of Al was added. the stoichiometric ratio of silicon and graphite has been deviated from that for Ti3SiC2. More Si and less graphite were needed to prepare a monolithic Ti3Si(Al)C-2 solid solution with high Al content. (c) 2005 Elsevier Ltd. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/34690] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | H. B. Zhang,Y. C. Zhou,Y. W. Bao,et al. Intermediate phases in synthesis of Ti3SiC2 and Ti3Si(Al)C-2 solid solutions from elemental powders[J]. Journal of the European Ceramic Society,2006,26(12):2373-2380. |
APA | H. B. Zhang,Y. C. Zhou,Y. W. Bao,M. S. Li,&J. Y. Wang.(2006).Intermediate phases in synthesis of Ti3SiC2 and Ti3Si(Al)C-2 solid solutions from elemental powders.Journal of the European Ceramic Society,26(12),2373-2380. |
MLA | H. B. Zhang,et al."Intermediate phases in synthesis of Ti3SiC2 and Ti3Si(Al)C-2 solid solutions from elemental powders".Journal of the European Ceramic Society 26.12(2006):2373-2380. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论