	Initial atmospheric corrosion of zinc in presence of Na2SO4 and (NH4)(2)SO4
	Q. Qu ; L. Li ; W. Bai ; C. W. Yan
刊名	Transactions of Nonferrous Metals Society of China
	2006
卷号	16 期号:4 页码:887-891
关键词	zinc Na2SO4 (NH4)(2)SO4 atmospheric corrosion sulfur-dioxide nacl so2 deposition
ISSN号	1003-6326
中文摘要	Initial atmospheric corrosion of zinc in the presence of Na2SO4 and (NH4)(2)SO4 was investigated via quartz crystal microbalance(QCM) in laboratory at relative humidity(RH) of 80% and 25 degrees C. The results show that both Na2SO4 and (NH4)(2)SO4 can accelerate the initial atmospheric corrosion of zinc. The combined effect of Na2SO4 and (NH4)2SO4 on the corrosion of zinc is greater than that caused by (NH4)(2)SO4 and less than that caused by Na2SO4. Fourier transform infrared spectroscopy(FTIR), X-ray diffractometry(XRD) and scanning electron microscopy(SEM) were used to characterize the corrosion products of zinc. (NH4)(2)Zn(SO4)(2), Zn4SO4(OH)(6)center dot 5H(2)O and ZnO present on zinc surface in the presence of (NH4)(2)SO4 while Zn4SO4(OH)(6)center dot 5H(2)O and ZnO are the dominant corrosion products on Na2SO4-treated zinc surface. Probable mechanisms are presented to explain the experimental results.
原文出处	://WOS:000240509600026
公开日期	2012-04-14
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/34438]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Q. Qu,L. Li,W. Bai,et al. Initial atmospheric corrosion of zinc in presence of Na2SO4 and (NH4)(2)SO4[J]. Transactions of Nonferrous Metals Society of China,2006,16(4):887-891.
APA	Q. Qu,L. Li,W. Bai,&C. W. Yan.(2006).Initial atmospheric corrosion of zinc in presence of Na2SO4 and (NH4)(2)SO4.Transactions of Nonferrous Metals Society of China,16(4),887-891.
MLA	Q. Qu,et al."Initial atmospheric corrosion of zinc in presence of Na2SO4 and (NH4)(2)SO4".Transactions of Nonferrous Metals Society of China 16.4(2006):887-891.