	Microstructural relationships between compounds in the Ti-Si-C system
	Z. J. Lin ; M. J. Zhuo ; Y. C. Zhou ; M. S. Li ; J. Y. Wang
刊名	Scripta Materialia
	2006
卷号	55 期号:5 页码:445-448
关键词	Ti(3)SiC(2) Ti(5)Si(3) TiC orientation relationship TEM titanium-silicon carbide orientation relationship elemental powders phase ti3sic2 mixture alloy
ISSN号	1359-6462
中文摘要	Microstructural relationships between Ti(5)Si(3) and TiC, and Ti(3)SiC(2) and TiC are reported. Ti5Si3 and TiC were determined to share a coherent interface following a new set of orientation relationships, i.e., (11 (2) over bar4)Ti(5)Si(3)\|\|(1 (1) over bar0)TiC and [22 (4) over bar(3) over bar ]Ti(5)Si(3)\|\|[110]TiC. Moreover, direct atomic resolution observation through Z-contrast scanning transmission electron microscopy showed that Ti3SiC2 nucleated within TiC. The close microstructural relationships between compounds in the Ti-Si-C system benefit the understanding of the reaction mechanism for the synthesis of Ti(3)SiC(2). (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
原文出处	://WOS:000239132200007
公开日期	2012-04-13
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/34335]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Z. J. Lin,M. J. Zhuo,Y. C. Zhou,et al. Microstructural relationships between compounds in the Ti-Si-C system[J]. Scripta Materialia,2006,55(5):445-448.
APA	Z. J. Lin,M. J. Zhuo,Y. C. Zhou,M. S. Li,&J. Y. Wang.(2006).Microstructural relationships between compounds in the Ti-Si-C system.Scripta Materialia,55(5),445-448.
MLA	Z. J. Lin,et al."Microstructural relationships between compounds in the Ti-Si-C system".Scripta Materialia 55.5(2006):445-448.