Nanometer martensite flakes in high-temperature deformation-induced ferrite grains of a low-carbon steel

CORC > 金属研究所 > 中国科学院金属研究所

	Nanometer martensite flakes in high-temperature deformation-induced ferrite grains of a low-carbon steel
	Z. X. Liu ; D. Z. Li ; G. W. Qiao ; Y. Y. Li
刊名	Scripta Materialia
	2007
卷号	56 期号:9 页码:777-780
关键词	nanometer martensite high-temperature deformation-induced ferrite carbon supersaturation low-carbon steel carbon diffusion strain-induced transformation austenite epma
ISSN号	1359-6462
中文摘要	High-temperature deformation-induced ferrite grains supersaturated with carbon offer superior properties such as higher elastic modulus and microhardness compared with procutectoid ferrite because of they contain nanometer martensite flakes. After annealing at 700 degrees C, fine carbides precipitate due to the decomposition of these nanometer martensite flakes. (c) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
原文出处	://WOS:000245157300014
公开日期	2012-04-13
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/33731]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Z. X. Liu,D. Z. Li,G. W. Qiao,et al. Nanometer martensite flakes in high-temperature deformation-induced ferrite grains of a low-carbon steel[J]. Scripta Materialia,2007,56(9):777-780.
APA	Z. X. Liu,D. Z. Li,G. W. Qiao,&Y. Y. Li.(2007).Nanometer martensite flakes in high-temperature deformation-induced ferrite grains of a low-carbon steel.Scripta Materialia,56(9),777-780.
MLA	Z. X. Liu,et al."Nanometer martensite flakes in high-temperature deformation-induced ferrite grains of a low-carbon steel".Scripta Materialia 56.9(2007):777-780.