Effect of pre-strain and two-step aging on microstructure and stress corrosion cracking of 7050 alloy | |
D. Wang ; D. R. Ni ; Z. Y. Ma | |
刊名 | Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
![]() |
2008 | |
卷号 | 494期号:1-2页码:360-366 |
关键词 | Aluminum Stress corrosion cracking Heat treatment Pre-Strain Grain boundary mg-cu alloy aluminum-alloy hydrogen embrittlement mechanical-properties scc-resistance strength precipitation aa7050 |
ISSN号 | 0921-5093 |
中文摘要 | A novel heat treatment procedure that combines the pre-strain with a two-step aging was proposed to improve both the strength and stress corrosion cracking (SCC) resistance of the high strength 7050 aluminum alloy. The heat treatment included a post-quenching pre-strain of 5%, a high-temperature aging at 200 degrees C for several minutes, and a subsequent low-temperature aging at 120 degrees C for 24h. The yield strength of the samples aged at 200 degrees C for 0.5 and 1 min was higher than that of the T6 sample. The SCC resistance of these samples was improved compared to the T6 sample, due to the enlargement in the size and the inter-particle distance of the grain boundaries precipitates and the decreases in the number of the GP zone. Especially, the sample aged at 200 degrees C for 5 min exhibited a similar SCC resistance and much higher elongation compared the T76 sample. (C) 2008 Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/33117] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | D. Wang,D. R. Ni,Z. Y. Ma. Effect of pre-strain and two-step aging on microstructure and stress corrosion cracking of 7050 alloy[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2008,494(1-2):360-366. |
APA | D. Wang,D. R. Ni,&Z. Y. Ma.(2008).Effect of pre-strain and two-step aging on microstructure and stress corrosion cracking of 7050 alloy.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,494(1-2),360-366. |
MLA | D. Wang,et al."Effect of pre-strain and two-step aging on microstructure and stress corrosion cracking of 7050 alloy".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 494.1-2(2008):360-366. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论