Influence of water vapor on the oxidation behavior of Ti3AlC2 and Ti2AlC

CORC > 金属研究所 > 中国科学院金属研究所

	Influence of water vapor on the oxidation behavior of Ti3AlC2 and Ti2AlC
	Z. J. Lin ; M. S. Li ; J. Y. Wang ; Y. C. Zhou
刊名	Scripta Materialia
	2008
卷号	58 期号:1 页码:29-32
关键词	Ti2AlC Ti3AlC2 water vapor oxidation microstructure high-temperature oxidation liquid reaction synthesis iron-chromium alloys oxide scale air deposition mechanism phase films tem
ISSN号	1359-6462
中文摘要	The influence of water vapor on the oxidation of Ti3AlC2 and Ti2AlC (TACs) was investigated at 500-1200 degrees C in controlled humidity atmospheres. Breakaway oxidation occurred in wet atmospheres at 500-600 degrees C because water vapor induced cracks in the oxide scales and prevented the formation of a protective Al2O3 scale. At elevated temperatures, water vapor slightly accelerated the oxidation of TACs due to the enhanced mass transportation process through the increased oxygen vacancy. (C) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
原文出处	://WOS:000251031600008
公开日期	2012-04-13
内容类型	期刊论文
源URL	[http://210.72.142.130/handle/321006/32929]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Z. J. Lin,M. S. Li,J. Y. Wang,et al. Influence of water vapor on the oxidation behavior of Ti3AlC2 and Ti2AlC[J]. Scripta Materialia,2008,58(1):29-32.
APA	Z. J. Lin,M. S. Li,J. Y. Wang,&Y. C. Zhou.(2008).Influence of water vapor on the oxidation behavior of Ti3AlC2 and Ti2AlC.Scripta Materialia,58(1),29-32.
MLA	Z. J. Lin,et al."Influence of water vapor on the oxidation behavior of Ti3AlC2 and Ti2AlC".Scripta Materialia 58.1(2008):29-32.