Low-temperature instability of Ti(2)SnC: A combined transmission electron microscopy, differential scanning calorimetry, and x-ray diffraction investigations | |
J. Zhang ; B. Liu ; J. Y. Wang ; Y. C. Zhou | |
刊名 | Journal of Materials Research |
2009 | |
卷号 | 24期号:1页码:39-49 |
关键词 | liquid reaction synthesis thin-films oxidation behavior thermal-stability phase-stability whisker growth m2snc m ti3sic2 ti2alc al |
ISSN号 | 0884-2914 |
中文摘要 | Transmission electron microscopy (TEM), differential scanning calorimetry (DSC), and x-ray diffraction (XRD) investigations were conducted oil the hot-pressed Ti(2)SnC bulk ceramic. Microstructure features of bulk Ti(2)SnC ceramic were characterized by using TEM, and a needle-shaped beta-Sn precipitation was observed inside Ti(2)SnC grains with the orientation relationship: (0001) Ti(2)SnC // (200) Sn and [1 (2) over bar 10] Ti(2)SnC // [001] Sn. With the combination of DSC and XRD analyses, the precipitation of metallic Sri was demonstrated to be a thermal stress-induced process during the cooling procedure. The reheating temperature, even as low as 400 degrees C, Could trigger the precipitation of Sn from Ti(2)SnC, which indicated the low-temperature instability of Ti(2)SnC. A substoichiometry Ti(2)Sn(x)C formed after depiction of Sn from ternary Ti(2)SnC phase. Under electron beam irradiation, metallic Sri was observed diffusing back into Ti(2)Sn(x)C. Furthermore, a new Ti(7)SnC(6) phase with the lattice constants of a = 0.32 and c = 4.1 nm was identified and added in the Ti-Sn-C ternary system. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/32546] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | J. Zhang,B. Liu,J. Y. Wang,et al. Low-temperature instability of Ti(2)SnC: A combined transmission electron microscopy, differential scanning calorimetry, and x-ray diffraction investigations[J]. Journal of Materials Research,2009,24(1):39-49. |
APA | J. Zhang,B. Liu,J. Y. Wang,&Y. C. Zhou.(2009).Low-temperature instability of Ti(2)SnC: A combined transmission electron microscopy, differential scanning calorimetry, and x-ray diffraction investigations.Journal of Materials Research,24(1),39-49. |
MLA | J. Zhang,et al."Low-temperature instability of Ti(2)SnC: A combined transmission electron microscopy, differential scanning calorimetry, and x-ray diffraction investigations".Journal of Materials Research 24.1(2009):39-49. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论