Effects of severe cold rolling on tensile properties and stress corrosion cracking of 7050 aluminum alloy | |
D. Wang ; Z. Y. Ma ; Z. M. Gao | |
刊名 | Materials Chemistry and Physics
![]() |
2009 | |
卷号 | 117期号:1页码:228-233 |
关键词 | Aluminum alloys Cold rolling Mechanical properties Stress corrosion cracking mg-cu alloy hydrogen embrittlement mechanical-properties pre-strain microstructure strength precipitation dislocations resistance |
ISSN号 | 0254-0584 |
中文摘要 | 7050 aluminum alloy samples were subjected to severe cold rolling (CR) deformation after solution treatment, and then were aged at conventional T6-aging temperature. After CR, shear bands appeared in the matrix and became wide with increasing the CR reduction. The strength of the 7050 samples increased with increasing the CR reduction. The yield and ultimate strengths of the CR sample with a reduction of 67% increased by 16.5% and 9.2%, respectively, compared to those of the T6 sample. Both the residual dislocations and heterogeneously nucleated fine eta' phase particles in the matrix increased the strength of the CR samples. Furthermore, the enlargement in the size and particle interval of the grain boundary precipitates improved the stress corrosion crack (SCC) resistance of the CR samples compared to that of the T6 sample. (c) 2009 Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/32342] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | D. Wang,Z. Y. Ma,Z. M. Gao. Effects of severe cold rolling on tensile properties and stress corrosion cracking of 7050 aluminum alloy[J]. Materials Chemistry and Physics,2009,117(1):228-233. |
APA | D. Wang,Z. Y. Ma,&Z. M. Gao.(2009).Effects of severe cold rolling on tensile properties and stress corrosion cracking of 7050 aluminum alloy.Materials Chemistry and Physics,117(1),228-233. |
MLA | D. Wang,et al."Effects of severe cold rolling on tensile properties and stress corrosion cracking of 7050 aluminum alloy".Materials Chemistry and Physics 117.1(2009):228-233. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论