Oxidation Behavior of Graded NiCrAlYRe Coatings at 900, 1000 and 1100 A degrees C | |
X. Liu ; L. Huang ; Z. Bao ; H. Wei ; X. Sun ; H. Guan ; Z. Hu | |
刊名 | Oxidation of Metals |
2009 | |
卷号 | 71期号:3-4页码:125-142 |
关键词 | Rhenium Oxidation alpha-Al(2)O(3) theta-Al(2)O(3) Phase transformation cyclic-oxidation alloys rhenium microstructure implantation improvement resistance additions growth scale |
ISSN号 | 0030-770X |
中文摘要 | A graded NiCrAlYRe coating was prepared by combining arc ion plating (AIP) with chemical vapor deposition (CVD) aluminizing. Quasi-isothermal oxidation tests of the graded NiCrAlYRe coating and the conventional NiCrAlYRe coating were performed in air at 900, 1000 and 1100 A degrees C for up to 1000, 1000 and 200 h, respectively. The results showed that the graded NiCrAlYRe coating exhibited better long time oxidation resistance than the conventional NiCrAlRe coating. This favorable oxidation behavior was attributed to the rapid formation of a protective alpha-Al(2)O(3) scale and a sufficient Al reservoir. The structures and morphologies of oxide scales varied under different oxidation conditions. theta-Al(2)O(3) was observed on both coatings during oxidation at 900 A degrees C, however, the graded coating showed more favorable conditions for theta-Al(2)O(3) to grow than the conventional coating. For the graded coating, phase transformation from theta-Al(2)O(3) to alpha-Al(2)O(3) resulted in a sharp decrease in the parabolic rate constant k(p) between 900 and 1,000 A degrees C. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/32112] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | X. Liu,L. Huang,Z. Bao,et al. Oxidation Behavior of Graded NiCrAlYRe Coatings at 900, 1000 and 1100 A degrees C[J]. Oxidation of Metals,2009,71(3-4):125-142. |
APA | X. Liu.,L. Huang.,Z. Bao.,H. Wei.,X. Sun.,...&Z. Hu.(2009).Oxidation Behavior of Graded NiCrAlYRe Coatings at 900, 1000 and 1100 A degrees C.Oxidation of Metals,71(3-4),125-142. |
MLA | X. Liu,et al."Oxidation Behavior of Graded NiCrAlYRe Coatings at 900, 1000 and 1100 A degrees C".Oxidation of Metals 71.3-4(2009):125-142. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论