Tensile and Fracture Behavior of DZ68 Ni-base Superalloy | |
E. Z. Liu ; S. C. Sun ; G. F. Tu ; Z. Zheng ; X. R. Guan ; L. F. Zhang | |
刊名 | Journal of Materials Science & Technology
![]() |
2009 | |
卷号 | 25期号:6页码:727-730 |
关键词 | Ni-base superalloy Tensile strength Yield strength Fractograph high-volume fraction temperature-dependence yield stress alloys deformation gamma' ni3al |
ISSN号 | 1005-0302 |
中文摘要 | The tensile and fracture behavior of DZ68 directionally solidified Ni-base superalloy was studied in the temperature range of room temperature (RT) to 1000 degrees C. The fracture mode was examined by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results show the tensile strength and yield strength of DZ68 alloy increase slightly with increasing temperature, so that at 760 degrees C its reach maxima value: 1214 and 1019 MPa, respectively. When the experimental temperature is higher than 760 degrees C, the tensile and yield strengths decrease evidently and the ductility increases remarkably. The fractograph of fracture surface for the tensile specimen at room temperature shows a dimple-ductile fracture mode. The fractograph from 760 to 850 degrees C shows a slide fracture mode. The fractograph from 900 to 1000 degrees C exhibits a creep rupture mode with uneven deformation. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/32074] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | E. Z. Liu,S. C. Sun,G. F. Tu,et al. Tensile and Fracture Behavior of DZ68 Ni-base Superalloy[J]. Journal of Materials Science & Technology,2009,25(6):727-730. |
APA | E. Z. Liu,S. C. Sun,G. F. Tu,Z. Zheng,X. R. Guan,&L. F. Zhang.(2009).Tensile and Fracture Behavior of DZ68 Ni-base Superalloy.Journal of Materials Science & Technology,25(6),727-730. |
MLA | E. Z. Liu,et al."Tensile and Fracture Behavior of DZ68 Ni-base Superalloy".Journal of Materials Science & Technology 25.6(2009):727-730. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论