Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime | |
Y. D. Li ; Z. G. Yang ; S. X. Li ; Y. B. Liu ; S. M. Chen ; W. J. Hui ; Y. Q. Weng | |
刊名 | Advanced Engineering Materials
![]() |
2009 | |
卷号 | 11期号:7页码:561-567 |
关键词 | subsurface crack initiation long cycle fatigue n-greater-than-10(7) cycles gigacycle fatigue assisted cracking part ii mechanism failure life inclusions |
ISSN号 | 1438-1656 |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/32046] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Y. D. Li,Z. G. Yang,S. X. Li,et al. Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime[J]. Advanced Engineering Materials,2009,11(7):561-567. |
APA | Y. D. Li.,Z. G. Yang.,S. X. Li.,Y. B. Liu.,S. M. Chen.,...&Y. Q. Weng.(2009).Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime.Advanced Engineering Materials,11(7),561-567. |
MLA | Y. D. Li,et al."Effect of Hydrogen on Fatigue Strength of High-Strength Steels in the VHCF Regime".Advanced Engineering Materials 11.7(2009):561-567. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论