Influence of NaCl deposition on atmospheric corrosion behavior of AZ91 magnesium alloy | |
W. Q. Zhou ; D. Y. Shan ; E. H. Han ; W. Ke | |
刊名 | Transactions of Nonferrous Metals Society of China
![]() |
2010 | |
卷号 | 20页码:S670-S673 |
关键词 | magnesium alloy atmospheric corrosion NaCl deposition X-ray photo electron spectroscopy chloride humidity |
ISSN号 | 1003-6326 |
中文摘要 | Corrosion behavior of AZ91 magnesium alloy under NaCl particle deposition condition was investigated by gravimetric method and surface analysis technique. It was found that the mass gain increased rapidly at the beginning of exposure and then slowly with time. The corrosion morphologies were observed and the results showed that NaCl deposition resulted in the occurrence of localized corrosion. The composition of corrosion product was analyzed using X-ray photo electron spectroscopy. It was suggested that the corrosion product was a mixture of oxide and hydroxide of magnesium and aluminum. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/31779] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | W. Q. Zhou,D. Y. Shan,E. H. Han,et al. Influence of NaCl deposition on atmospheric corrosion behavior of AZ91 magnesium alloy[J]. Transactions of Nonferrous Metals Society of China,2010,20:S670-S673. |
APA | W. Q. Zhou,D. Y. Shan,E. H. Han,&W. Ke.(2010).Influence of NaCl deposition on atmospheric corrosion behavior of AZ91 magnesium alloy.Transactions of Nonferrous Metals Society of China,20,S670-S673. |
MLA | W. Q. Zhou,et al."Influence of NaCl deposition on atmospheric corrosion behavior of AZ91 magnesium alloy".Transactions of Nonferrous Metals Society of China 20(2010):S670-S673. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论