Corrosion behaviour of sol-gel coatings doped with cerium salts on 2024-T3 aluminum alloy | |
H. W. Shi ; F. C. Liu ; E. H. Han | |
刊名 | Materials Chemistry and Physics
![]() |
2010 | |
卷号 | 124期号:1页码:291-297 |
关键词 | Electrochemical impedance spectroscopy Sol-gel coatings Corrosion X-ray photoelectron spectroscopy self-healing properties galvanized steel silane solutions protection inhibition pretreatments spectroscopy |
ISSN号 | 0254-0584 |
中文摘要 | The corrosion behaviour of the sol-gel coatings doped with cerium chloride or cerium nitrate on 2024-T3 aluminum alloy was investigated by using electrochemical impedance spectroscopy (EIS) and immersion tests. The sol-gel matrix was obtained through hydrolysis, condensation of 3-glycidoxypropyltrimethoxysilane (GPTMS) and tetramethoxysilane (TMOS), using diethylentriamine as curing agent. The results indicated that cerium nitrate with concentration of 1 x 10(-3) mol L(-1) in the silane solution was excellent on self-healing for the sol-gel coating, while cerium chloride had no obvious effect. This result suggested that the introduction of Cl(-) promoted the under-film pitting of 2024-T3 substrate. It was found that Ce(OH)(3) and Ce(OH)(2)(2+) simultaneously existed in the silane solution by X-ray diffraction (XRD) analysis. Ce(OH)(2)(2+) transformed to CeO(2) due to high-temperature curing of sol-gel matrix demonstrated by X-ray photoelectron spectroscopy (XPS) analysis. Therefore, it can be considered that Ce(OH)(3) and CeO(2) played inhibition roles in the corrosion process of the sol-gel coatings. (C) 2010 Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/31437] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | H. W. Shi,F. C. Liu,E. H. Han. Corrosion behaviour of sol-gel coatings doped with cerium salts on 2024-T3 aluminum alloy[J]. Materials Chemistry and Physics,2010,124(1):291-297. |
APA | H. W. Shi,F. C. Liu,&E. H. Han.(2010).Corrosion behaviour of sol-gel coatings doped with cerium salts on 2024-T3 aluminum alloy.Materials Chemistry and Physics,124(1),291-297. |
MLA | H. W. Shi,et al."Corrosion behaviour of sol-gel coatings doped with cerium salts on 2024-T3 aluminum alloy".Materials Chemistry and Physics 124.1(2010):291-297. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论