Hydrothermal Oxidation Behavior of Bulk Titanium Aluminum Carbide

CORC > 金属研究所 > 中国科学院金属研究所

	Hydrothermal Oxidation Behavior of Bulk Titanium Aluminum Carbide
	H. B. Zhang ; V. Presser ; K. G. Nickel ; C. Berthold ; Y. C. Zhou
刊名	Journal of the American Ceramic Society
	2011
卷号	94 期号:10 页码:3460-3466
关键词	ti3si0.9al0.1c2 solid-solution silicon-carbide m(n+1)ax(n) phases supercritical water ti3sic2 powders thin-film ti3alc2 carbon ceramics temperatures
ISSN号	0002-7820
中文摘要	Hydrothermal oxidation of bulk Ti(3)AlC(2) in continuous water flow was studied at 500 degrees-700 degrees C under a hydrostatic pressure of 35 MPa. During hydrothermal oxidation, titanium and aluminum were oxidized and selectively removed from Ti(3)AlC(2) with the survival of carbon. Reaction kinetics obeyed a linear time-law. The hydrothermal oxidation rates were sluggish at 500-600 degrees C and faster at 700 degrees C accompanied with the formation of cracks in oxides. This study clarified that the resistance of bulk Ti(3)AlC(2) against hydrothermal oxidation was high up to 700 degrees C.
原文出处	://WOS:000295524300056
公开日期	2012-04-13
内容类型	期刊论文
源URL	[http://210.72.142.130/handle/321006/30876]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	H. B. Zhang,V. Presser,K. G. Nickel,et al. Hydrothermal Oxidation Behavior of Bulk Titanium Aluminum Carbide[J]. Journal of the American Ceramic Society,2011,94(10):3460-3466.
APA	H. B. Zhang,V. Presser,K. G. Nickel,C. Berthold,&Y. C. Zhou.(2011).Hydrothermal Oxidation Behavior of Bulk Titanium Aluminum Carbide.Journal of the American Ceramic Society,94(10),3460-3466.
MLA	H. B. Zhang,et al."Hydrothermal Oxidation Behavior of Bulk Titanium Aluminum Carbide".Journal of the American Ceramic Society 94.10(2011):3460-3466.