Corrosion resistant performance of a chemical quenched rebar in concrete | |
J. Wei ; J. H. Dong ; W. Ke | |
刊名 | Construction and Building Materials |
2011 | |
卷号 | 25期号:3页码:1243-1247 |
关键词 | Rebar Surface state EIS Corrosion resistance Concrete reinforcing steel passive film neutral solution iron spectroscopy bars |
ISSN号 | 0950-0618 |
中文摘要 | The corrosion resistance performance of the rebar quenched by a new chemical reagent FM in concrete containing chloride ions was evaluated comparing with bare rebar, water-cooled rebar and air-cooled rebar using electrochemical methods. Two different accelerated corrosion tests (14 cycles of dry/wet alternated corrosion tests and long-term immersion tests) were carried out to accelerate the corrosion process. EIS results of both accelerated corrosion tests showed the corrosion resistance performance of different rebar specimens could be sequenced from high to low as FM-cooled rebar, bare rebar, air-cooled rebar, and water-cooled rebar. It was observed that, after 14 cycles of accelerated corrosion tests, the corrosion degree of FM-cooled rebar is the slightest and most of the initial scale remains undamaged. This result proves that the corrosion resistance of the FM-cooled rebar is much better than the other three kinds of rebar. By using FM-cooling process, the corrosion resistance performance of rebar in concrete has been improved by optimizing the quality of the scale. (C) 2010 Elsevier Ltd. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/30767] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | J. Wei,J. H. Dong,W. Ke. Corrosion resistant performance of a chemical quenched rebar in concrete[J]. Construction and Building Materials,2011,25(3):1243-1247. |
APA | J. Wei,J. H. Dong,&W. Ke.(2011).Corrosion resistant performance of a chemical quenched rebar in concrete.Construction and Building Materials,25(3),1243-1247. |
MLA | J. Wei,et al."Corrosion resistant performance of a chemical quenched rebar in concrete".Construction and Building Materials 25.3(2011):1243-1247. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论