Cyclic oxidation behavior of glass-ceramic composite coatings on superalloy K38G at 1100 degrees C | |
M. L. Shen ; S. L. Zhu ; F. H. Wang | |
刊名 | Thin Solid Films |
2011 | |
卷号 | 519期号:15页码:4884-4888 |
关键词 | Glass-ceramic coating NiCoCrAlY Cyclic oxidation Magnetron sputtering resistance microstructure scales |
ISSN号 | 0040-6090 |
中文摘要 | The SiO(2)-Al(2)O(3)-ZrO(2)-CaO-ZnO glass-ceramic composite coatings (GC), nanocrystalline NiCoCrAlY coating, and their combinations (bi-layer GC/NiCoCrAlY) were prepared on K38G specimens. The thicknesses of the glass-ceramic coatings and the NiCoCrAlY coatings were about 10 mu m and 20 mu m, respectively. Cyclic oxidation tests were carried out at 1100 degrees C for 120 cycles. Microstructures of the specimens before and after oxidation tests were characterized by SEM, EDS and XRD. The glass-ceramic coatings with or without a NiCoCrAlY intermediate layer improved the isothermal and cyclic oxidation resistance of the Ni-base superalloy K38G at 1100 degrees C, and performed better than the NiCoCrAlY coatings. An alumina layer formed at the glass/metal interfaces of the specimens coated by the glass-ceramic coatings with or without a NiCoCrAlY intermediate layer. The NiCoCrAlY intermediate layer was beneficial to the cyclic oxidation resistance of the glass-ceramic coatings. (C) 2011 Elsevier B.V. All rights reserved. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://210.72.142.130/handle/321006/30649] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | M. L. Shen,S. L. Zhu,F. H. Wang. Cyclic oxidation behavior of glass-ceramic composite coatings on superalloy K38G at 1100 degrees C[J]. Thin Solid Films,2011,519(15):4884-4888. |
APA | M. L. Shen,S. L. Zhu,&F. H. Wang.(2011).Cyclic oxidation behavior of glass-ceramic composite coatings on superalloy K38G at 1100 degrees C.Thin Solid Films,519(15),4884-4888. |
MLA | M. L. Shen,et al."Cyclic oxidation behavior of glass-ceramic composite coatings on superalloy K38G at 1100 degrees C".Thin Solid Films 519.15(2011):4884-4888. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论