Structural Evolution of a Colloidal Crystal Fiber during Heating and Annealing Studied by in Situ Synchrotron Small Angle X-ray Scattering | |
Hu SS ; Rieger J ; Yi ZY ; Zhang JQ ; Chen XL ; Roth SV ; Gehrke R ; Men YF | |
刊名 | langmuir
![]() |
2010 | |
卷号 | 26期号:16页码:13216-13220 |
关键词 | LATEX FILM FORMATION ATOMIC-FORCE MICROSCOPY CORE-SHELL LATEX POLYMER DIFFUSION INTERDIFFUSION RATES ENERGY-TRANSFER METHACRYLATE) PARTICLES SURFACE |
ISSN号 | 0743-7463 |
通讯作者 | men yf |
中文摘要 | the structural evolution of a colloidal crystal fiber during heating and annealing was followed by in situ synchrotron small-angle x-ray scattering. the polymer dispersion (with a particle size of 118 nm) from which the fibers were formed by directed drying contained emulsifier and salt. a cellular structure formed upon drying in which the percolating phase (the "membrane phase") is composed from these components; this membrane phase gives rise to the scattering contrast on which the present observations build. changes of the lattice constant of the colloidal crystallites and the intensity evolution of the scattering from the crystalline and the amorphous phases during heating and annealing indicate characteristic temperatures where the system exhibits pronounced structural changes. the first characteristic temperature was identified as 125 degrees c above which residue water in the membrane material was evaporated leading to shrinkage of the colloidal crystalline lattice. at a temperature above about 140 degrees c the membrane material was expelled out of the crystalline domains. this effect is accompanied by the progressive interdiffusion of polymer chains between adjacent latex particles and leads to further thermal shrinkage of the colloidal crystals. the second characteristic temperature is defined by a rapid increase in isotropic scattering. this effect is attributed to the formation of increasingly large domains of the membrane material and the concomitant disappearance of the membrane phase from the former crystal domains. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000280667900028 |
公开日期 | 2012-04-26 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/43534] ![]() |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Hu SS,Rieger J,Yi ZY,et al. Structural Evolution of a Colloidal Crystal Fiber during Heating and Annealing Studied by in Situ Synchrotron Small Angle X-ray Scattering[J]. langmuir,2010,26(16):13216-13220. |
APA | Hu SS.,Rieger J.,Yi ZY.,Zhang JQ.,Chen XL.,...&Men YF.(2010).Structural Evolution of a Colloidal Crystal Fiber during Heating and Annealing Studied by in Situ Synchrotron Small Angle X-ray Scattering.langmuir,26(16),13216-13220. |
MLA | Hu SS,et al."Structural Evolution of a Colloidal Crystal Fiber during Heating and Annealing Studied by in Situ Synchrotron Small Angle X-ray Scattering".langmuir 26.16(2010):13216-13220. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论