	Si与Mg含量对离心铸造原位颗粒增强Al-xSi-yMg复合材料组织与耐磨性能的影响 Effects of Si and Mg contents on the structures and wear resistance of centrifugal AI- xSi -yMg composites reinforced with in situ particles
	林雪冬[1,2]; 刘昌明[1]; 吕循佳[1]
	2013
卷号	30页码:155-164
URL标识	查看原文
内容类型	期刊论文
URI标识	http://www.corc.org.cn/handle/1471x/2991385
专题	重庆大学
推荐引用方式 GB/T 7714	林雪冬[1,2],刘昌明[1],吕循佳[1]. Si与Mg含量对离心铸造原位颗粒增强Al-xSi-yMg复合材料组织与耐磨性能的影响 Effects of Si and Mg contents on the structures and wear resistance of centrifugal AI- xSi -yMg composites reinforced with in situ particles[J],2013,30:155-164.
APA	林雪冬[1,2],刘昌明[1],&吕循佳[1].(2013).Si与Mg含量对离心铸造原位颗粒增强Al-xSi-yMg复合材料组织与耐磨性能的影响 Effects of Si and Mg contents on the structures and wear resistance of centrifugal AI- xSi -yMg composites reinforced with in situ particles.,30,155-164.
MLA	林雪冬[1,2],et al."Si与Mg含量对离心铸造原位颗粒增强Al-xSi-yMg复合材料组织与耐磨性能的影响 Effects of Si and Mg contents on the structures and wear resistance of centrifugal AI- xSi -yMg composites reinforced with in situ particles".30(2013):155-164.

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。