Origin of the modulus anomaly over a wide temperature range of Mn0.70Fe0.25Cu0.05 alloy | |
Cui, Yanguang; Guo, Yunlong; Li, Yangxin; Wan, Jianfeng; Zhang, Jihua; Rong, Yonghua; Chen, Nailu; Wang, Dong; Wang, Yunzhi | |
刊名 | COMPUTATIONAL MATERIALS SCIENCE
![]() |
2017 | |
卷号 | 140页码:89-94 |
关键词 | Modulus anomaly Antiferromagnetic transition Phase-field method |
ISSN号 | 0927-0256 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2942000 |
专题 | 西安交通大学 |
推荐引用方式 GB/T 7714 | Cui, Yanguang,Guo, Yunlong,Li, Yangxin,et al. Origin of the modulus anomaly over a wide temperature range of Mn0.70Fe0.25Cu0.05 alloy[J]. COMPUTATIONAL MATERIALS SCIENCE,2017,140:89-94. |
APA | Cui, Yanguang.,Guo, Yunlong.,Li, Yangxin.,Wan, Jianfeng.,Zhang, Jihua.,...&Wang, Yunzhi.(2017).Origin of the modulus anomaly over a wide temperature range of Mn0.70Fe0.25Cu0.05 alloy.COMPUTATIONAL MATERIALS SCIENCE,140,89-94. |
MLA | Cui, Yanguang,et al."Origin of the modulus anomaly over a wide temperature range of Mn0.70Fe0.25Cu0.05 alloy".COMPUTATIONAL MATERIALS SCIENCE 140(2017):89-94. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论