	Hot-corrosion behavior of a La2Ce2O7/YSZ thermal barrier coating exposed to Na2SO4+V2O5 or V2O5 salt at 900 degC
	Wang, X.a,b; Guo, L.c,d; Peng, H.a,b; Zheng, L.a,b; Guo, H.a,b; Gong, S.a,b
刊名	Ceramics International
卷号	Vol.41 No.5页码:6604-6609
ISSN号	0272-8842
URL标识	查看原文
内容类型	期刊论文
URI标识	http://www.corc.org.cn/handle/1471x/2898623
专题	天津大学
作者单位	1.aSchool of Materials Science and Engineering, Beihang University, China 2.bBeijing Key Laboratory of Advanced Functional Materials and Thin Film Technology, Beihang University, No. 37 Xueyuan Road, Beijing, 100191, China 3.cSchool of Materials Science and Engineering, Tianjin University, China 4.dTianjin Key Laboratory of Advanced Joining Technology, Tianjin University, No. 92, Weijin Road, Tianjin, 300072, China
推荐引用方式 GB/T 7714	Wang, X.a,b,Guo, L.c,d,Peng, H.a,b,et al. Hot-corrosion behavior of a La2Ce2O7/YSZ thermal barrier coating exposed to Na2SO4+V2O5 or V2O5 salt at 900 degC[J]. Ceramics International,Vol.41 No.5:6604-6609.
APA	Wang, X.a,b,Guo, L.c,d,Peng, H.a,b,Zheng, L.a,b,Guo, H.a,b,&Gong, S.a,b.
MLA	Wang, X.a,b,et al."Hot-corrosion behavior of a La2Ce2O7/YSZ thermal barrier coating exposed to Na2SO4+V2O5 or V2O5 salt at 900 degC".Ceramics International Vol.41 No.5