Investigation on Viscosity and Nonisothermal Crystallization Behavior of P-Bearing Steelmaking Slags with Varying TiO2 Content | |
Wang, Zhanjun ; Sun, Yongqi ; Sridrar, Seetharaman ; Zhang, Mei ; Zhang, Zuotai | |
刊名 | METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE
![]() |
2017 | |
关键词 | STEEL SLAG SILICATE-GLASSES MOLD FLUXES PHOSPHORUS PHASE SYSTEM TEMPERATURE ENRICHMENT KINETICS FLUORIDE |
DOI | 10.1007/s11663-016-0825-4 |
英文摘要 | The viscous flow and crystallization behavior of CaO-SiO2-MgO-Al2O3-FetO-P2O5-TiO2 steelmaking slags have been investigated over a wide range of temperatures under Ar (High purity, > 99.999 pct) atmosphere, and the relationship between viscosity and structure was determined. The results indicated that the viscosity of the slags slightly decreased with increasing TiO2 content. The constructed nonisothermal continuous cooling transformation (CCT) diagrams revealed that the addition of TiO2 lowered the crystallization temperature. This can mainly be ascribed to that addition of TiO2 promotes the formation of [TiO6]-octahedra units and, consequently, the formation of MgFe2O4-Mg2TiO4 solid solution. Moreover, the decreasing viscosity has a significant effect on enhancing the diffusion of ion units, such as Ca2+ and [TiO4]-tetrahedra, from bulk melts to the crystal-melt interface. The crystallization of CaTiO3 and CaSiTiO5 was consequently accelerated, which can improve the phosphorus content in P-enriched phase (n2CaO center dot SiO2-3CaO center dot P2O5). Finally, the nonisothermal crystallization kinetics was characterized and the activation energy for the primary crystal growth was derived such that the activation energy increases from -265.93 to -185.41 KJ center dot mol(-1) with the addition of TiO2 content, suggesting that TiO2 lowered the tendency for the slags to crystallize. (C) The Minerals, Metals & Materials Society and ASM International 2016; National Natural Science Foundation of China [51522401, 51472007, 51372019]; National High Technology Research and Development Program of China (863 Program) [2012AA06A114]; SCI(E); ARTICLE; 1; 527-537; 48 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/475534] ![]() |
专题 | 工学院 |
推荐引用方式 GB/T 7714 | Wang, Zhanjun,Sun, Yongqi,Sridrar, Seetharaman,et al. Investigation on Viscosity and Nonisothermal Crystallization Behavior of P-Bearing Steelmaking Slags with Varying TiO2 Content[J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE,2017. |
APA | Wang, Zhanjun,Sun, Yongqi,Sridrar, Seetharaman,Zhang, Mei,&Zhang, Zuotai.(2017).Investigation on Viscosity and Nonisothermal Crystallization Behavior of P-Bearing Steelmaking Slags with Varying TiO2 Content.METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE. |
MLA | Wang, Zhanjun,et al."Investigation on Viscosity and Nonisothermal Crystallization Behavior of P-Bearing Steelmaking Slags with Varying TiO2 Content".METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE (2017). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论