High temperature flexural strength of B4C-ZrB2 ceramic at 1000-1600 degrees C in air | |
Cheng, Xiangmeng ; He, Rujie ; Qu, Zhaohang ; Ai, Shigang ; Fang, Daining | |
刊名 | CERAMICS INTERNATIONAL
![]() |
2015 | |
关键词 | Mechanical properties B4C High temperature Oxidation MECHANICAL-PROPERTIES B4C CERAMICS COMPOSITES DENSIFICATION MICROSTRUCTURE OXIDATION SIZE |
DOI | 10.1016/j.ceramint.2015.07.174 |
英文摘要 | B4C-30 vol% ZrB2 ceramic was prepared using hot pressing. The room temperature and high temperature flexural strength of the as-prepared ceramic were investigated. The room temperature flexural strength was measured to be 604.5 MPa. When the ceramic was tested at 1000 degrees C, the flexural strength kept nearly the same as room temperature flexural strength, because no serious oxidation happens and the oxide product can heal the cracks on the surface. When the temperature was above 1000 degrees C, oxidation becomes severer and the mechanical properties decrease sharply. The flexural strength at 1200, 1400 and 1600 degrees C is 451.5, 287.5 and 202.5 MPa, respectively. Microstructure evolution of the B4C-ZrB2 ceramic was also investigated. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.; China Postdoctoral Science Foundation [2014M550558, 2015T80018]; National Natural Science Foundation of China [11402003, 11227801]; SCI(E); ARTICLE; herujie@pku.edu.cn; sgai@pku.edu.cn; 10; 14574-14578; 41 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/415257] ![]() |
专题 | 工学院 |
推荐引用方式 GB/T 7714 | Cheng, Xiangmeng,He, Rujie,Qu, Zhaohang,et al. High temperature flexural strength of B4C-ZrB2 ceramic at 1000-1600 degrees C in air[J]. CERAMICS INTERNATIONAL,2015. |
APA | Cheng, Xiangmeng,He, Rujie,Qu, Zhaohang,Ai, Shigang,&Fang, Daining.(2015).High temperature flexural strength of B4C-ZrB2 ceramic at 1000-1600 degrees C in air.CERAMICS INTERNATIONAL. |
MLA | Cheng, Xiangmeng,et al."High temperature flexural strength of B4C-ZrB2 ceramic at 1000-1600 degrees C in air".CERAMICS INTERNATIONAL (2015). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论