Crystallization Behaviors of Slags through a Heat Flux Simulator | |
Ryu, H. G. ; Zhang, Z. T. ; Cho, J. W. ; Wen, G. H. ; Sridhar, S. | |
刊名 | isij international
![]() |
2010 | |
关键词 | mold slag TRIP steel crystallization behavior heat flux MOLD FLUX STEELS TRANSFORMATION POWDERS CAF2 |
DOI | 10.2355/isijinternational.50.1142 |
英文摘要 | This paper investigates how the basicity and alumina content in synthetic slags influence the crystallization behavior that takes place in a heat flux simulator for mold slags. The purpose is to elucidate the variation in crystallization behavior for model slags that are expected to be glassy, partly crystalline and fully crystalline in order to correlate the changes in heat flux to the dynamic solid evolution that occurs in the simulator. Three levels of alumina content (3, 15 and 25 wt%) were chosen to investigate the heat transfer behavior through slag film which have different tendency of reaction with molten steel during continuous casting of high aluminum containing Transformation Induced Plasticity (TRIP) steels. A Confocal Scanning Laser Microscopy (CSLM) was used to develop TTT diagrams for the slags. XRD and SEM were also used to analyze the micro-structures of the crystalline phases. The measured heat fluxes through the mold slags tested were found to increase, as the crystallinity of the slag film decreased with decreasing basicity and alumina content. It was found that the crystallization temperature increased, while the incubation time for crystallization decreases with increasing basicity and alumina content. The increase in alumina content induced the precipitation of CaF(2) during cooling process and hence a change in the crystalline phase from Ca(4)Si(2)O(7)F(2) to Ca(2)Al(2)SiO(7).; Metallurgy & Metallurgical Engineering; SCI(E); EI; 23; ARTICLE; 8; 1142-1150; 50 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/396018] ![]() |
专题 | 工学院 |
推荐引用方式 GB/T 7714 | Ryu, H. G.,Zhang, Z. T.,Cho, J. W.,et al. Crystallization Behaviors of Slags through a Heat Flux Simulator[J]. isij international,2010. |
APA | Ryu, H. G.,Zhang, Z. T.,Cho, J. W.,Wen, G. H.,&Sridhar, S..(2010).Crystallization Behaviors of Slags through a Heat Flux Simulator.isij international. |
MLA | Ryu, H. G.,et al."Crystallization Behaviors of Slags through a Heat Flux Simulator".isij international (2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论